Abstract:In this work, we propose a simple and efficient interfacial modification method for thin-film transistor (TFT)-1 with poor stability under bias stress. For conventional top-contact TFT-2, the sputtering passivation layer will cause the device to be in a short-circuit condition. We used inverted coplanar-structured TFT-3 to separate the high conductivity layer from the S/D electrodes to avoid the short-circuit failure of the device, but this will cause a hump effect. Ultraviolet treatment and air annealing were performed on TFT-3 simultaneously to obtain TFT-4 with high mobility (μsat = 45.5 cm2 V–1 s–1), steep subthreshold swing (SS = 86 mV/dec), and good bias stability (±20 V, 3600 s, NBS: −0.1 V, PBS: +0.9 V, PGDBS: +0.5 V). The forward and reverse tests of TFT-1 and TFT-4 after the PGDBS test show that TFT-4 has a good stability of the asymmetric electrical bias. Finally, XRR, XPS, AFM, and contact angle were tested to further investigate the material mechanisms. In this paper, we show that the interfacial passivation of TFT can effectively isolate the invasion of external water/oxygen and compensate for interfacial defects and dangling bonds. The decomposition and rearrangement of the oxide are induced by UV + thermal annealing, which optimizes the stacking pattern of the cells, effectively reducing the defect states and eliminating parasitic channels and the hump phenomenon. Finally, an amorphous oxide semiconductor (AOS)-TFT instrument with high mobility and good stability is prepared. The method in this paper addresses the problem that the passivation layer cannot be prepared by sputtering, which is a cost-effective process.

Hybrid-Phase Microstructural ITO-Stabilized ZnO TFTs with Self-Aligned Coplanar Architecture

Scalability and Stability Enhancement in Self-Aligned Top-Gate Indium- Zinc-Oxide TFTs with Al Reacted Source/Drain

High mobility of IGO/IGZO double-channel thin-film transistors by atomic layer deposition

Solution-processed Coplanar Top-Gate ZnInSnO Thin Film Transistors and Bias Stability

Self-Aligned Top-Gate Amorphous InGaZnO TFTs with Plasma Enhanced Chemical Vapor Deposited Sub-10 Nm SiO2 Gate Dielectric for Low-Voltage Applications

Enhanced Stability Performance of Transparent Ozone ALD ZnO Thin-Film Transistors with SiAlOX Dielectric

Mobility and Stability Enhancement of Amorphous In-Ga-Zn-O TFTs with Atomic Layer Deposited Al2O3/SiO2Stacked Insulators

High-Performance Flexible ZnO Thin-Film Transistors by Atomic Layer Deposition

Enhancing the Stability and Mobility of TFTs via Indium-Tungsten Oxide and Zinc Oxide Engineered Heterojunction Channels Annealed in Oxygen Ambient

Back-End-of-Line Compatible InSnO/ZnO Heterojunction Thin-Film Transistors With High Mobility and Excellent Stability

The Hump Phenomenon and Instability of Oxide TFT Were Eliminated by Interfacial Passivation and UV + Thermal Annealing Treatment

Fabrication and Properties of InGaZnO Thin-Film Transistors Based on a Sol–Gel Method with Different Electrode Patterns

High-Performance Unannealed A-Ingazno Tft with an Atomic-Layer-Deposited Sio2 Insulator

Teflon/SiO2 Bilayer Passivation for Improving the Electrical Reliability of Oxide TFTs Fabricated Using a New Two-Photomask Self-Alignment Process

Self-Aligned Top-Gate Amorphous Zinc-Tin Oxide Thin-Film Transistor with Source/Drain Regions Doped by Al Reaction

High Reliability Of Igzo Tfts Using Low-Temperature Fabricated Organic Passivation Layers

Amorphous NdIZO Thin Film Transistors with Contact-Resistance-Adjustable Cu S/D Electrodes

Vertical Oxide Homojunction TFTs of 0.8 V Gated by $ \hbox{h}_{3}\hbox{po}_{4}$ -Treated $\hbox{sio}_{2}$ Nanogranular Dielectric

Enhanced performances of a-IGZO TFTs with oxide passivation layers fabricated by hollow cathode assisted PLD

Enhanced Electrical and Mechanical Performance of InSnZnO TFTs With Multifunctional Laminated Organic Passivation Layer

Amorphous indium–gallium–zinc–oxide thin-film transistors using organic–inorganic hybrid films deposited by low-temperature plasma-enhanced chemical vapor deposition for all dielectric layers