Abstract:Complex characteristics of the pores and properties of porous reaction-bonded Si3N4 have been investigated and correlated with the microstructure of Si3N4 grains. Porous ceramics with porosities of ≤ 75 vol% and α-Si3N4 matte grains (α/β phase ratio of 1.5) or α-Si3N4 whiskers (α/β phase ratio of 0.36) were prepared by in situ nitridation of silicon powder. To obtain various microstructures by α → β-phase transformation and grain morphology modification, samples were heat-treated at 1700 °C while embedded in a Si3N4 powder bed containing MgO. By the growth of α-matte or β-Si3N4 grains on the pore walls, highly interconnected structures with spherical cavities and unimodal pore size distributions resulted with d50 ≈ 8.8 µm and ≈ 6.5 µm, respectively. In contrast, α-whiskers grew inside the pore cavities; thus, complex and irregular inter-particle pores appeared which generated an extra peak near d50 ≈ 1 µm forming a bimodal pore size distribution. Compared to the α-matte grains, α-whiskers densified upon heat treatment and produced a large drop in porosity, which resulted in a structure with less interconnectivity. As a consequence of growth of fine β-rods, pore walls became relatively smooth and whisker free; thus, inter-cluster channels were modified to spherical cavities with d50 ≈ 3.7 µm. Samples exhibiting networked whiskers and fine pores or low porosity demonstrated higher compressive strength than the interconnected structures with spherical cavities.

Extrusion of Highly Porous Silicon Nitride Ceramics with Bimodal Pore Structure and Improved Gas Permeability

Porous Silicon Nitride Ceramics Prepared By Extrusion Process

Processing, microstructure and mechanical properties of porous silicon nitride by a slip casting method-using petroleum coke as pore former

Preparation and Characterization of Porous Si3N4 Ceramics Prepared by Compression Molding and Slip Casting Methods

Gas permeability and mechanical properties of porous alumina ceramics with unidirectionally aligned pores

Pore structure, porosity and compressive strength of highly porous reaction-bonded silicon nitride ceramics with various grain morphologies

Fabrication of High-Porosity Silicon Nitride Ceramics with Excellent Mechanical Properties

Simultaneous improvement in porosity and strength of porous β-Si3N4 ceramics by formation of ultrafine fibrous grains

Porous Silicon Nitride Ceramics Prepared by Extrusion Using Starch as Binder

Porous Silicon Nitride Ceramics Prepared by Reduction-Nitridation of Silica

Manufacture of Si3N4-SiCN composite bulks with hierarchical pore structure

Fabrication of Porous Silicon Nitride with High Porosity by Diatomite

Porous silicon nitride and SiAlON ceramics: Fabrication and characterization

Fabrication of continuously porous SiC–Si3N4 composite using SiC powder by extrusion process

Effects of Pore Morphology on the Fabrication and Mechanical Properties of Porous Si<sub>3</sub>N<sub>4</sub> Ceramics

Fabrication of Gradient Porous SiC Ceramics with Directional Pores Without Templates

Effects of pore morphology on the fabrication and mechanical properties of porous Si3N4 ceramics

Permeating behaviour of porous SiC ceramics fabricated with different SiC particle sizes

Porous 2h‐silicon Carbide Ceramics Fabricated by Carbothermal Reaction Between Silicon Nitride and Carbon

Synthesis of Fibrous Β-Si3n4 Structured Porous Ceramics Using Carbothermal Nitridation of Silica