Abstract:To realize cost-effectively manufacture of high-performance Si3N4 porous ceramic, a ferrosilicon nitride porous ceramic with an optimized interlocking structure was synthesized by flash combustion synthesis using FeSi75 powder as raw material. And the technology has been improved in many ways to ensure stable industrial production. The theoretical combustion temperature of FeSi75 in N2(g) is up to 4608K, while Si3N4 is unstable. Both adding diluent and designing the preheat temperature of nitrogen are taken to control synthesis temperature below 1600 °C. During synthesis, the Fe–Si liquid phase and SiO(g), which are essential for the selective growth of elongated columnar β-Si3N4 and whisker α-Si3N4 respectively, are formed firstly. Then, nitriding proceed in multiple ways. N diffuses through Fe–Si(l) and reacts with Si to form β-Si3N4, and the growth of elongated β-Si3N4 in Fe–Si liquid follows the dynamic ripening model, which is very fast and effective. Thus, an interlocking structure composed of elongated β-Si3N4 with an aspect ratio above 20 is reached. There is also an indirect nitridation reaction, that is, FeSi75 preferentially reacts with trace O2 in atmosphere to form SiO(g), which is further nitrided to form needle-like α-Si3N4. Needle-like α-Si3N4 is interspersed in the well-developed columnar β-Si3N4, making the structure stronger. Fe finally exists in the form of Fe3Si, which binds the surrounding elongated Si3N4 to form a sea-urchin like unit, making the structure more stable and strengthened. Through control of these reactions, optimizations in microstructure are reached, and the annual output of has reached 25,000 tons. The reaction model is established.

Synthesis of Fibrous Β-Si3n4 Structured Porous Ceramics Using Carbothermal Nitridation of Silica

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Biomimetic Synthesis of Porous Si_3N_4 Ceramics

Synthesis and Mechanical Properties of Highly Porous Ultrafine-Grain Si3N4 Ceramics Via Carbothermal Reduction-Nitridation Combined with Liquid Phase Sintering

Porous Silicon Nitride Ceramics Fabricated by Carbothermal Reduction-Reaction Bonding

Synthesis of Porous Silicon Nitride Ceramics from Diatomite

Fabrication and Strengthening of Porous Si3N4 Ceramics by Replacement of Oxide Phase with Si3N4 at Grain Boundary Through Carbothermal Nitridation

Simultaneous improvement in porosity and strength of porous β-Si3N4 ceramics by formation of ultrafine fibrous grains

Porous 2h‐silicon Carbide Ceramics Fabricated by Carbothermal Reaction Between Silicon Nitride and Carbon

Microstructure Control and Mechanical Properties of Porous Silicon Nitride Ceramics

Biomorphic Silicon Nitride Ceramics with Fibrous Morphology Prepared by Sol Infiltration and Reduction–Nitridation

Preparation of Porous Si3N4 Ceramics with Controlled Porosity and Microstructure by Fibrous Α‐si3n4 Addition

Effects of α-Si3N4 seeds and sintering additives on properties of porous silicon nitride ceramics fabricated by carbothermal reduction

Synthesis and properties of porous SiN/SiC nanocomposites by carbothermal reaction between SiN and carbon

Porous Silicon Nitride Ceramics Prepared by Reduction-Nitridation of Silica

Fabrication and Mechanical Properties of Porous Silicon Nitride Ceramics from Low-Purity Powder

Facile Fabrication of Nanofibrous Network Reinforced Hierarchical Structured Porous Si3N4-based Ceramics Based on Si-Si3N4 Binary Particle-Stabilized Foams

Porous Silicon Nitride Ceramics Prepared by Carbothermal Reduction Method

Fabrication of High-Porosity Silicon Nitride Ceramics with Excellent Mechanical Properties

Cost-effective manufacture and synthesis mechanism of ferrosilicon nitride porous ceramic with interlocking structure

Effect of Pure Β-Si3n4powder on Microstructure and Mechanical Properties of Porous Si3N4ceramics