Abstract:In this work, the effects of Nb2O5 addition on the dielectric properties and phase formation of BaTiO3 were investigated. A core–shell structure was formed for Nb-doped BaTiO3 resulted from a low diffusivity of Nb5+ ions into BaTiO3 when grain growth was inhibited. In the case of 0.3–4.8 mol% Nb2O5 additions, two dielectric constant peaks were observed. The Curie dielectric peak was determined by the ferroelectric-paraelectric transition of grain core, whereas the secondary broad peak at lower temperature was due to strong chemical inhomogeneity in Nb-doped BaTiO3 ceramics. The dielectric constant peak at Curie temperature was markedly depressed with the addition of Nb2O5. On the other hand, the secondary dielectric constant peak was enhanced when sintered above 1280 °C for higher Nb2O5 concentrations (≥1.2 mol%). The Curie temperature was shifted to higher temperatures, whereas the transition temperature corresponding to the secondary peak moved to lower temperatures as increasing the amount of Nb2O5 more than 1.2 mol%. The decrease of this lower transition temperature was assumed to be closely related with the secondary phase formation when Nb concentration greater than 1.2 mol%. From XRD analyses, a large amount of secondary phases was observed when Nb2O5 amount exceeded 1.2 mol%. The coefficients of thermal expansion of Nb-doped BaTiO3 were increased with increasing Nb2O5 contents, resulting in large internal stress between cores and shells. Therefore, the shift of Curie temperature to higher temperatures was attributed to internal stress resulting from the formation of a core–shell structure and a large amount of secondary phase grains.

Enhanced Dielectric Properties in (in, Nb) Co-Doped BaTiO3 Ceramics

Colossal Dielectric Permittivity in (al+nb) Co-Doped Ba0.4Sr0.6TiO3 Ceramics

The Dielectric Properties for (nb,in,b) Co-Doped Rutile TiO2 Ceramics

Dielectric behaviors of Nb2O5–Co2O3 doped BaTiO3–Bi(Mg1/2Ti1/2)O3 ceramics

Structural, Electrical, Magnetic and Optical Properties of BaTi1−x(Ni1/2Nb1/2)xO3 Ceramics

Effect of Na0.5Bi0.5TiO3 on Dielectric Properties of BaTiO3 Based Ceramics

Structural Evolution and Dielectric Properties of Nd and Mn Co-Doped BaTiO3 Ceramics

Investigation on dielectric properties of BaTiO3 co-doped with Ni and Nb

Synthesis and characterization of BaTiO 3-(Bi 0.5Na 0.5)TiO 3 solid solution based dielectric ceramics

The effect of co-substitution on the microwave dielectric properties of Ba6-3Nd8+2Ti18O54(x=2/3) ceramics

Improved Dielectric and Energy Storage Properties of Ba0.8Ca0.2TiO3 Ceramics by Doping Ba(Mg1/3Nb2/3)O3

Investigation of the modulation effects of BiNbO4 doping on BaTiO3-based ceramics

Colossal dielectric behavior and relaxation in Nd-doped BaTiO 3 at low temperature

Doping Behaviors of Nb2O5 and Co2O3 in Temperature Stable BaTiO3-based Ceramics

Effects of W,Ti Co-Doping on the Microstructure and Microwave Dielectric Properties of Ba5nb4o15 Ceramics

The effect of doping process on microstructure and dielectric properties of BaTiO 3 -based X7R materials

Effects of Nb 2 O 5 Doping on the Microstructure and the Dielectric Temperature Characteristics of Barium Titanate Ceramics

Colossal Permittivity in Niobium Doped BaTiO3 Ceramics Annealed in N-2

Dielectric properties of bismuth doped Ba1-xCaxTiO3 ceramics

Effects of neodymium doping on dielectricand optical properties of Ba (1-x)NdxTi1.005O3

Electrical Properties and Microstructures of (zn and Nb) Co-Doped BaTiO3 Ceramics Prepared by Microwave Sintering