Improvement in the Sintering and Electrical Properties of Strontium- and Magnesium-Doped Lanthanum Gallate by MoO3 Dopant

Yuan Wang,De Feng Zhou,Lei Chen,Shen Kun Xie,Xiao Juan Liu,Jian Meng
DOI: https://doi.org/10.1016/j.jallcom.2017.03.323
IF: 6.2
2017-01-01
Journal of Alloys and Compounds
Abstract:The LSGM powders by doping 0-2.5 at.% of MoO3 were synthesized and investigated. The microstructure and electrical properties of the samples were characterized by X-ray diffraction (XRD), field-emission scanning electron microscopy (FE-SEM) and electrochemical impedance spectroscopy (EIS) respectively. The results showed that the phase purity, densification and conductivity of the LSGM samples could be improved by a proper addition of MoO3. The LSGM specimen by doping 2 at.% MoO3 exhibited the best phase purity, the best density, the largest grain size and the lowest activation energy. Moreover, it was found that the conductivity of the LSGM by doping 2 at.% MoO3 was 3.91 x 10(-4) S cm(-1) at 450 degrees C, which was 2.82 times as high as LSGM without MoO3 doping. Moreover, the thermal expansion coefficient of the LSGM-2Mo sample changed little by MoO3 doping. Therefore, the MoO3 doped LSGM may be a potential electrolyte material for anode-supported solid oxide fuel cells (SOFCs) without requiring buffer layer between anode and electrolyte. (C) 2017 Elsevier B.V. All rights reserved.
What problem does this paper attempt to address?