Abstract:Solid-state electrolytes are key materials for developing high-safety solid-state Li-ion batteries. The garnet-type Li7La3Zr2O12 (LLZO) solid electrolyte is one of the most promising solid electrolytes due to its high conductivity and feasible preparation in ambient air. Among several dopants, Ta-doped LLZO (Ta-LLZO) delivers high stability against lithium metal and high conductivity, which attracts lots of researchers. However, production of Ta-LLZO ceramics is less problematic due to the complicated gas–liquid–solid sintering mechanism. This work aims to develop an efficient method to produce Ta-LLZO solid electrolyte ceramic pellets, including providing a stacking sintering method and optimizing the amount of excessive Li source, the wet milling duration, and the sintering temperature. First, a low-cost, efficient “gravel-separator” strategy is provided for multiple sintering of LLZO. Second, the Li6.5La3Zr1.5Ta0.5O12 (Ta5) samples with different excessive Li levels (2, 4, 6, and 8%) are sintered at various sintering conditions of 1240 °C for 60 min, 1280 °C for 20 min, and 1320 °C for 2 min to search for the optimum excessive amount of Li. Third, Ta5 samples with optimized excessive Li (4, 6%) after milling for longer duration are sintered at 1280 °C for 30 min, 1300 °C for 10 min, 1320 °C for 10 min, 1320 °C for 30 min to finally optimize the preparation craft. After optimization, the Ta5 ceramics with excessive 4 and 6% Li sintered at 1320 °C for 10 min deliver homogeneous and dense cross-sectional morphology, high conductivity of over 1 × 10–3 S cm–1 at room temperature, and relative densities of above 96%. Furthermore, symmetric Li cells assembled with the Ta-LLZO solid electrolyte prepared with the optimized method deliver a critical current density of 1.28 mA cm–2 at 30 °C and over 1000 h of stable cycling at 0.2 mA cm–2 (0.2 mA h cm–2) at 30 °C.

Sintering mechanism and greatly enhanced ionic conductivity of Mo-doped Li7La3Zr2O12 ceramics via a novel covered sintering

Manipulating Li2O atmosphere for sintering dense Li7La3Zr2O12 solid electrolyte

Developing Preparation Craft Platform for Solid Electrolytes Containing Volatile Components: Experimental Study of Competition between Lithium Loss and Densification in Li7La3Zr2O12

Rapid sintering method for highly conductive Li7La3Zr2O12 ceramic electrolyte

Preparation of dense Ta-LLZO/MgO composite Li-ion solid electrolyte: Sintering, microstructure, performance and the role of MgO

In-situ Li2O-atmosphere Assisted Solvent-Free Route to Produce Highly Conductive Li7La3Zr2O12 Solid Electrolyte

Key factors of the self-consolidation mechanism for sintering Li7La3Zr2O12 solid electrolytes

Synergetic Effect of Li-Ion Concentration and Triple Doping on Ionic Conductivity of Li7La3Zr2O12 Solid Electrolyte

Amorphous Dual‐Layer Coating: Enabling High Li‐Ion Conductivity of Non‐Sintered Garnet‐Type Solid Electrolyte

Broad temperature dependence, high conductivity, and structure-property relations of cold sintering of LLZO-based composite electrolytes

Preparation and performances of gallium-doped LLZO electrolyte with high ionic conductivity by rapid ultra-high-temperature sintering

Improvement of Ionic Conductivity in Li7La3Zr2O12 (LLZO) Solid Electrolyte By Doping with Aluminum/Tungsten

Production of Ta-Doped Li 7 La 3 Zr 2 O 12 Solid Electrolyte with High Critical Current Density

Rapid Fabrication of of Li7La3Zr2O12 Solid Electrolyte with Enhanced Lithium Ionic Conductivity by Microwave Sintering

The Synergistic Effects of Dual Substitution of Bi and Ce on Ionic Conductivity of Li7La3Zr2O12 Solid Electrolyte

Influence of Dry‐ and Wet‐milled LLZTO Particles on the Sintered Pellets

Formation Mechanism of Sol-Gel Synthesized Li7−3Al La3Zr2O12 and the Influence of Abnormal Grain Growth on Ionic Conductivity

On the Interfacial Properties of the Garnet-Type Electrolyte Ceramic Pellets of Cubic Li6.4la3zr1.4ta0.6o12: A Comprehensive Promotion Mechanism by the Sintering Additive of Li-Ion Conducting Licl

Fast and low-temperature densification of highly conductive Li7La3Zr2O12 ceramic electrolytes for solid-state batteries

Self-consolidation Mechanism and Its Application in the Preparation of Al-doped Cubic Li7La3Zr2O12