Abstract:Thick high-strength steel plates are increasingly being used for ship structures. Moreover, hydrogen enters the process of manufacturing and service, and large residual tensile stress occurs near the weld. Such stress can facilitate the diffusion and accumulation of hydrogen in the material, leading to hydrogen embrittlement fracture of the shell. Therefore, residual-stress-induced diffusion and accumulation of hydrogen in the stress concentration region of thick butt-welded high-strength steel plate structures need to be studied. In this study, manual metal arc welding was realized by numerical simulation of residual stress in a thick butt-welded high-strength steel plate model using the thermoelastic–plastic theory and a double ellipsoidal heat source model. To analyze residual stress, a set of numerical simulation methods was obtained through comparative analysis of the test results of relevant literature. Residual and hydrostatic stress distributions were determined based on these methods. Then, hydrogen diffusion parameters in each region of the model were obtained through experimental tests. Finally, the results of the residual stress field were used as the predefined field of hydrogen diffusion to conduct a numerical simulation analysis. The distribution of hydrogen diffusion under the influence of residual stress was obtained based on the theory of stress-induced hydrogen diffusion. The weak area of the welding joint was found to be near the weld toe, which exhibited high hydrostatic stress and hydrogen concentration. Further, the maximum hydrogen concentration value of the vertical weld path was approximately 6.1 ppm, and the maximum value of the path parallel to the weld centerline and 31 mm away from the weld centerline was approximately 6.22 ppm. Finally, the hydrostatic tensile stress in the vertical weld path was maximized (~345 MPa), degrading the material properties and causing hydrogen-related cracking. Hence, a reliable method for the analysis of hydrogen diffusion according to residual stress in thick high-strength steel plates was obtained. This work could provide a research basis for controlling and eliminating the adverse effects of hydrogen on the mechanical properties of ship structures and ensuring the safe service of marine equipment.

Finite Element Simulation of the Effect of Welding Residual Stress on Hydrogen Diffusion

3-D Finite Element Analysis of the Effect of Welding Residual Stress on Hydrogen Diffusion in Hydrogen Contained Environment

Numerical Simulation of Hydrogen Diffusion under Welding Residual Stress

3D FINITE ELEMENT SIMULATION OF HYDROGEN DIFFUSION IN 16mnr STEEL WELDMENT

Effect of Residual Stress on Hydrogen Diffusion in Thick Butt-Welded High-Strength Steel Plates

Numerical Simulation of Hydrogen Diffusion in Low Alloy Steel Welded Joint under Wet H2S Environment

Numerical Simulation on Hydrogen Induced Cracking Behavior of 4130X Hydrogen Storage Vessel with Defect

Effect of Residual Stress on Hydrogen Diffusion in Flat Butt Welding Joints

Finite Element Analysis of the Residual Stress and Distortion of the Welding of Hastelloy-C276 Alloy Pipes

Research on residual stress and hydrogen diffusion of X80 pipeline welded joint

Prediction of Residual Stress Distributions in Welded Sections of P92 Pipes with Small Diameter and Thick Wall Based on 3D Finite Element Simulation

Hydrogen diffusion simulation of the X80 pipeline steel girth weld zone considering the synergistic effect of the structure–stress–concentration field

FE analysis of residual stress and welding deformation of a low-alloy UHS quenched steel fillet joint

Finite Element Modeling of Hydrogen Diffusion in Fusion Zone of Hq130 High Strength Steel

Numerical Simulation Analysis of Welding Residual Stress on Dissimilar Metal Welded Pipes

Study on the Synergistic Effect of Welding Residual Stress and Hydrogen Diffusion on Fatigue Crack Growth of X80 Steel Pipeline

Multiphysics Study of Thermal Profiles and Residual Stress in Welding

Effect of Microstructure Inhomogeneity on Hydrogen Diffusion in 2.25Cr1Mo0.25V Welded Joints

INVESTIGATION OF HYDROGEN DIFFUSION CHARACTERISTICS OF THE HEAT AFFECTED ZONE OF 2.25CR-1MO-0.25V STEEL BY AN ELECTROCHEMICAL PERMEATION METHOD

Effect of Thermophysical Parameters on the Hump Feature of Welding Residual Stress by Finite Element Analysis

Numerical Simulation of Welding Residual Stress of Tube-to-tubesheet Joint in Heat Exchangers