Two Novel Low-Firing Germanates Li 2 MGe 3 O 8 (M = Ni, Co) Microwave Dielectric Ceramics with Spinel Structure

Hao Luo,Liang Fang,Huaicheng Xiang,Ying Tang,Chunchun Li

DOI: https://doi.org/10.1016/j.ceramint.2016.10.107

IF: 5.532

2016-01-01

Ceramics International

Abstract:Two low-firing ceramics Li2MGe3O8 (M = Ni, Co) were prepared using the solid state reaction method and their microwave dielectric properties were characterized. X-ray diffraction analysis showed that both ceramics crystallized into a cubic spinel structure. Both ceramics were well densified at temperatures lower than 960°C. Li2NiGe3O8 ceramic sintered at 940°C with relative density of ~95.2% obtained the optimum microwave dielectric properties with a relative permittivity (εr) ~8.6, a quality factor (Q×f) ~42,200GHz (at 12.2GHz), a temperature coefficient of resonance frequency τf ~ −78.2ppm/°C. For Li2CoGe3O8, the ceramic sintered at 950°C had a relative density of 95.4%, a εr of 9.0, a Q×f of 40,500GHz (at 12.6GHz) and a τf of −42ppm/°C. The negative τf values could be tuned by forming composite ceramics with rutile TiO2. Chemical compatibility measurement indicates that both ceramics did not react with silver.