Influences of soft chain segment on performance of PU dispersoid with high solid content based on amino-sulphonate

De-quan DONG,Dong-cheng SUN

DOI: https://doi.org/10.3969/j.issn.1004-2849.2009.11.005

2009-01-01

Abstract:With N-(2-aminoethyl)-2-aminoethane sulphonic sodium(AAS-Na) as hydrophile monomer,polyol with different structures,isophorone diisocyanate(IPDI),hexamethylene diisocyanate(HDI) and ethylene-diamine(EDA)as raw materials,so a polyurethane dispersoid(PUD) with 50% solid content was synthesized based on amino-sulphonate by acetone method.The research results showed that the PUD's characteristics were fake-plastic fluid,its zeta(ζ) potentials and viscosity were less than-30 mV and 800 mPa·s respectively,and average particle sizes were 230-290 nm.The PUD had well water resistance because water absorptions of PUD's films were less than 10%.The influences of soft chain segment were bigger on the crystallization behavior and mechanics performance of PUD films,its initial decomposed temperature was 275 ℃,so PUD had well heat stability and could met use request in common occasion.