Abstract:To achieve the high dispersion of SiO2 nanoparticles in polyurethane acrylate resin, the titanate coupling agent, PN-102, was used as the surface modifier to prepare the modified SiO2 nanoparticles (Si-PN102-5) with small particle size and good dispersion ability in PUA-6 resin. Accordingly, hydrophilic SiO2 (Si-380) and hydrophobic SiO2 (Si-115) were introduced into PUA-6 resin to prepare the corresponding composite coatings, so as to investigate the effects of SiO2 nanoparticles modified with different surface modifiers on the properties of PUA / SiO2 composite coatings. The properties of PUA / SiO2 composite coatings were characterized by the tests of FTIR, AFM, SEM, DMA, TG and so on. The FT-IR and XPS results show that PN-102 had functionalized the SiPN102-5 particle surface successfully. The TEM test displays that the particle size of SiO2 was almost unchanged before and after modification, maintaining at about 20-30 nm. The SEM, DMA and tensile test reveal that Si-PN102-5 not only blocks the interaction and accumulation of nanoparticles, but also enhances the interface interaction with polymer chains through chain entanglement, which endows Si-PN102-5-5% composite coatings with highest mechanical strength among the other prepared coatings, reaching to 11.0 +/- 0.1 MPa in tensile strength and 9.4 +/- 3.0% in elongation at break. The pencil hardness of the prepared Si-PN102-5-5% composite coating could reach to 5H which is higher than the commercial PUA-6 based coating, and it also displayed good adhesion (4B) and flexibility (3 mm). The TG results show that all of prepared composite coatings display good thermal stability with a decomposition temperature of higher than 250 degrees C.

Synthesis and Characteristics of Polyurethane-polyacrylate Composite Emulsion

Study on Silicone Modified Polyurethane-Acrylate Copolymer Emulstion

Preparation and Properties of High Solid Content and Low Viscosity Waterborne Polyurethane—Acrylate Emulsion with a Reactive Emulsifier

Polyurethane Acrylate Microgel Synthesized by Emulsion Polymerization Using Unsaturated Self-Emulsified Polymer

Preparation, mechanical properties of waterborne polyurethane and crosslinked polyurethane‐acrylate composite

Synthesis and Properties of Cationic Core-Shell Fluorinated Polyurethane Acrylate

Synthesis and Application of Hydroxyethyl Methacrylate Modified Waterborne Polyurethane

Preparation and Characterization of a Self -Matting Coating Based on Waterborne Polyurethane-Polyacrylate Hybrid Dispersions

Preparation and Properties of Phase‐change Heat‐storage UV Curable Polyurethane Acrylate Coating

Effects of aminopropyl-terminated polydimethylsiloxane on structure and properties of waterborne polyurethane-acrylate

THE SYNTHESIS AND CHARACTERIZATION OF POLYURETHANE-ACRYLIC GRAFT EMULSION

A crosslinked waterborne poly(urethane‐urea) oligomer enables mechanically strong waterborne polyacrylate–poly(urethane‐urea) hybrid films with superior film‐forming ability

Preparation, Characterization, and Property Analysis of Environmentally Friendly Waterborne Polyurethane-Acrylate

Preparation, properties and application of waterborne hydroxyl-functional polyurethane/acrylic emulsions in two-component coatings

Facile preparation of homogenous waterborne poly(urethane/acrylate) composites and the correlation between microstructure and improved properties

Hydrophobicity of Polyacrylate Emulsion Film Enhanced by Introduction of Nano-SiO₂ and Fluorine

Synthesis and characterization of waterborne polyurethane emulsions based on poly(butylene itaconate) ester

Research of Synthesis and Properties Anionic Water-Borne Polyurethane Type Polyether Emulsion

Synthesis and properties of epoxy resin modified solvent-free anionic polyurethane/polyacrylate composite emulsion

Preparation and Properties of UV-curable Polyurethane Acrylate/sio2 Composite Hard Coatings

Synthesis and properties of polyurethane modified with an aminoethylaminopropyl-substituted polydimethylsiloxane. II. Waterborne polyurethanes