Ultra-high Strength Steel Treated by Using Quenching–Partitioning–Tempering Process
T. Y. Hsu (Zuyao Xu),Xuejun Jin
DOI: https://doi.org/10.1007/978-3-642-17665-4_8
2011-01-01
Abstract:Quenching-Partitioning-Tempering (Q-P-T) process is developed to yield ultra-high strength and high toughness steel based on Q-P process suggested by Speer et al. The chemical composition of Q-P-T steel is designed as <0.5C, 1.5Si (or Al), 1.5Mn, 0.02Nb, 0.2Mo (mass%) in which complex carbide precipitation during tempering may contribute further hardening; or <0.5C, 1.5Si, 1.5Mn (mass%) in which eta(theta) carbide precipitation may offer strengthening beside the martensite formation. Ultimate tensile strength and total elongation of >2,000 MPa and >10%, similar to 1,500 MPa and similar to 15%, and similar to 900 MPa and similar to 20% are obtained with Q-T-P processed steels containing 0.4, 0.2 and 0.1C, respectively. Steels processed by Q-P-T generally contain similar to 5% retained austenite. Several examples are given in this article. The thermodynamics and kinetics as well as strengthening and toughing mechanisms for Q-P-T process are briefly discussed.