Synthesis of Polycarboxylate with Different Comb Structures and It's Influence on Properties of Fresh Cement Pastes

Shuncheng XIANG,Caijun SHI,Linmei WU,Lingling CHONG

DOI: https://doi.org/10.14062/j.issn.0454-5648.2015.05.04

2015-01-01

Abstract:Three polycarboxylates with different comb structures(i.e., the same degree of polymerization in main chains and different side chains) were synthesized via radical polymerization reaction. The effect of polycarboxylates on the surface tension and the fluidity in cement pastes was determined. The effect of polycarboxylates on the surface tension of liquid, the fluidity, and Zeta potential of cement pastes with different kinds and contents of mineral admixture were also investigated. The results show that the surface tension of polycarboxylate decreases from 47.70 m N/m to 35.53 m N/m and the paste fluidity increases from 280 mm to 310 mm with increasing the molar ratio between isoamyl alcohol polyoxyethylene(TPEG) and α-methacrylate(α-MAA) from 1:1 to 5:1. The liquid surface tension of cement pastes decreases and the paste fluidity increases with increasing the dosage of supplementary cementitious materials and polycarboxylate. As the water-cement ratio decreases from 0.5 to 0.3, the Zeta potential of cement pastes increases. When the water-cement ratio is 0.3, the Zeta potential decreases with increasing the dosage of supplementary cementitious materials and polycarboxylate.