Towards strength-ductility synergy through a novel technique of multi-pass lowered-temperature drawing in AZ31 magnesium alloys
Jingyuan Shen,Lingyu Zhang,Lianxi Hu,Wenchao Liu,Aiwei Fang,Zekun Yao,Yongquan Ning,Lili Ren,Yu Sun
DOI: https://doi.org/10.1016/j.jallcom.2021.159604
IF: 6.2
2021-08-01
Journal of Alloys and Compounds
Abstract:<p>Since the intrinsic brittleness of magnesium alloys critically hinders their applications, the enhancement in ductility of the alloys has become an unremittingly pursuing, let alone evade the strength-ductility trade-off dilemma. Here we unexpectedly prepared the high strength-ductility synergy magnesium alloy wires with the minimum diameter of 1.9 mm via multi-pass lowered-temperature drawing together with intermediate annealing. The results show that the weakened basal texture and refined grains were attributed to recrystallization, while the texture attribute, such as crystal orientation which rotated toward <span class="math"><math>〈101¯0〉−〈112¯0〉</math></span> arc from <span class="math"><math>〈112¯0〉</math></span> fiber and ultimately formed <span class="math"><math>〈101¯0〉</math></span> fiber as drawing proceeded, was dominantly induced by compatibility deformation arising from the activation of correlated deformation modes. The identification criteria that the percentages of participation of each deformation mode available at each λ were coincidence with the known mechanism that extension twin at 0° (λ), basal slip at 45° and prismatic slip at 90° were predominant, respectively. The premature yielding behavior could be evaded by inhibiting extensive <span class="math"><math>{101¯2}</math></span> twins so as to achieve high yield strength and the seamless transition between deformation modes gave rise to consecutive strain-hardening capacity, resulting in synchronous improvement of ultimate tensile stress and fracture elongation.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering