Abstract:The cold drawing of magnesium wires has constantly been an obstacle in industrial manufacture due to the lack of sufficient independent slip system at ambient temperature and the frequent intermediate annealing gives rise to regrettably low production efficiency. Aiming at the technique challenge, a feasible and effective method of multi-pass cumulative cold drawing with small deformation per pass was utilized in this study and a wire of 0.625mm in diameter was obtained out of primitive Φ2.0mm material with the accomplishment of about 2.3 in cumulative strain (90% in area reduction), the efficiency of which was dramatically improved. The microstructure, texture and mechanical properties with the variation of cumulative area reduction were investigated. It can be apparently observed that continuous dynamic recrystallization had occurred during cold drawing. The outcomes are displayed as follows: the transition emerged from low angle grain boundary to high angle grain boundary; the increased fraction of undeformed/recrystallized structure first descended then ascended; the deformed structure initially appeared yet disappeared quickly. All of above owned an almost same critical point at around 23% cumulative area reduction. One of the most remarkable consequences of the deformation was the degeneration of the average grain size steadily from 11.8 to 3.1µm. 〈10-10〉//DD fiber component was gradually transformed from the primitive {0002}//DD fiber texture and this deformation texture was continuously strengthened. The enhanced mechanical properties achieved uncommonly high strength of 214.5MPa in yield strength and 256.9MPa in ultimate tensile strength due to grain refinement arising from continuous dynamic recrystallization and intense fiber texture strengthening introduced during cold drawing.

Achieving Ultrafine Grain Size in Mg-Al-Zn Alloy by Cold Drawing

Working Hardening Behaviors of Severely Cold Deformed and Fine-Grained AZ31 Mg Alloys at Room Temperature

Microstructure Stability of Cold Drawn AZ31 Magnesium Alloy During Annealing Process

Influence of Large Cold Strain on the Microstructural Evolution for a Magnesium Alloy Subjected to Multi-Pass Cold Drawing

Superior Strength-Ductility Synergy of Mg-Nd-Zn-Zr Alloy Rod Achieved by Drawing at Elevated Temperatures

Effect of grain size distribution and texture on the cold extrusion behavior and mechanical properties of AZ31 Mg alloy

Microstructures, Textures and Mechanical Properties Evolution During Cold Drawing of Pure Mg

The effect of cold drawing on the structure, tensile fracture strength and reliability of CuZrAl amorphous microwires

EFFECT OF HEAVILY DRAWING ON THE MICROSTRUCTURE AND PROPERTIES OF Cu-Cr ALLOYS

Microstructure evolution and mechanical property of Mg-Gd-Y-Zn-Zr alloy wires prepared by hot drawing

Towards strength-ductility synergy through a novel technique of multi-pass lowered-temperature drawing in AZ31 magnesium alloys

Effect of Grain Boundary Segregation on Microstructure and Mechanical Properties of Ultra-Fine Grained Mg–Al–Ca–Mn Alloy Wires

Fine-grained Structure and Recrystallization at Ambient Temperature for Pure Magnesium Subjected to Large Cold Plastic Deformation

Effect of Cold Deformation on Microstructure and Mechanical Properties of Mg-8Gd-3Y-0.5Zr Alloy

Static recrystallization kinetics of a heavily cold drawn AZ31 magnesium alloy under annealing treatment

High strength high electrical conductivity ultrafine-grained Al–Y alloy processed via cold drawing

Grain refining and improving mechanical properties of AZ31 Mg alloy sheets by multi-pass warm rolling with falling temperature

The Effects of Grain Size on Ductility of AZ31 Magnesium Alloy

Phase transformation, texture evolution, and mechanical properties of Mg-9.5Gd-4Y-2Zn-0.3Zr alloy wires fabricated using hot drawing

Effect of Mg content on mechanical properties and electrical conductivity of ultrafine-grained Al–Mg–Zr wires produced by ECAP-Conform and drawing

Enhanced Strength‐Ductility Synergy of Mg‐6Zn Alloy Wire by Inducing GP Zone Precipitation