Abstract:Polycarbonate is a widely used ductile glassy polymer that can undergo large strain deformation before failure. During the plastic deformation process, some mechanical energy is converted to heat, which, if the specimen is loaded at rates sufficient that the heat cannot conduct out of the material, can result in significant temperature rises that affect the mechanical response. Typically, this is expected to result in a reduction in stress at large strain, compared to the behaviour under isothermal conditions; however, compared to other glassy polymers, it has been observed that less softening than expected is experienced in polycarbonate at high strain rates. The current paper describes a thorough investigation of temperature rises in polycarbonate. Compression experiments are performed using a screw-driven machine, a hydraulic machine, and a long split Hopkinson bar, all instrumented with a high-speed infrared camera to measure temperature rises at strain rates between 0.01 and 2600 s -1 at a starting temperature around 20°C. Further, temperature rises in compression experiments at 0.5 s -1 and starting temperatures between -80 to 150°C are measured using embedded thermocouples. These span the range of the secondary- to glass-transitions of polycarbonate, allowing investigation of the effect of these transitions. These experiments are supported by finite element simulations, which use a phenomenological viscoplastic model, to ensure the thermal boundary conditions are adiabatic. Temperature rises are observed in both temperature and rate-dependent tests: experiments at higher strain rates and lower temperatures experience a greater temperature rise because of the higher yield stress; however, there are differences in the conversion ratio between plastic work and heat (Taylor Quinney coefficient), which is both temperature and rate dependent, and strongly affected by both the secondary and glass transitions.

Delamination Cracking Mechanism of Polycarbonate Thin-Walled Componet

Study on Delamination Failure Mechanism of Polycarbonate Thin-Walled Component

Delamination of Plasticized Devices in Dynamic Service Environments

Thermal Degradation Behavior and Flame Retardancy of Polycarbonate Containing Poly[(phenylsilsesquioxane)-co-(dimethylsiloxane)] and Potassium Diphenyl Sulfonate

Effects of matrix cracks on delamination of composite laminates subjected to low-velocity impact

Degradation Behavior of Polycarbonate in Different Damp and Heat Natural Environments

Polycarbonate blends with high environmental stress crack resistance, high strength and high toughness by introducing polyvinyl butyral at small fraction

The Crystallinity of Pvc and Its Effect on Physical Properties

Simulation of Interfacial Delamination Crack of Waste Plastic Chips

Residual strength and failure mechanism of CF/PPS composites with delamination damage

The Influence of Environmental Stress Cracking (ESC) and Gamma Irradiation on the Mechanical Properties of Polycarbonate: Study of Synergistic Effects

The Analysis of Delamination and Fracture in IC Packages

Thermomechanical coupling during large strain deformation of polycarbonate: Experimental study

Competing Behavior of Interface Delamination and Wafer Cracking During Peeling Film from Ultra-Thin Wafer

Slow crack growth in polycarbonate films

A study on environmental stress cracking in nano-SiO2-filled polycarbonate

Preparation and characterization of long chain branched polycarbonates with significantly enhanced environmental stress cracking behavior through gamma radiation with addition of difunctional monomer

A Review of Delamination Damage of Composite Materials

Interlaminar Stress and Damage Mechanism of Thermoplastic Composite Laminates

The effect of delamination on damage behavior of composite laminates subjected to three-point bending

Concentration Dependence of Crystallinity of Polycarbonate by Shock-Cooling and Subsequent Freeze-Drying of Its Various Solutions