Effect of Pre-strain on Hot Ductility of Nb-microalloyed 09mnnidr Cryogenic Steel

LI Jian-hua,WU Kai-ming,QIU Jin-ao

2012-01-01

Abstract:The effect of tensile pre-strain on the hot ductility of the Nb-microalloyed 09MnNiDR cryogenic steel was investigated by examining microstructures of the tensile fracture using optical microscopy and electron microscopy,and by measuring the reduction of area.When 5% tensile pre-strain was applied at 800℃,the microstructure was composed of ferrite grains and lots of grain boundary ferrite allotriomorphs along grain boundaries,the reduction of area being 63%.When it was applied at 900℃,the microstructure was composed of bainite,acicular ferrite and lots of massive grain boundary carbonitrides,the reduction of area falling to 35%.When it was applied at 1000℃ the microstructure mainly consisted of lath-like martensite,the reduction of area climbing up to 95%.Comparing with the specimens without applying pre-strain,the reduction of area of the specimens applied with pre-strain between 800℃ and 920℃ dropped remarkably.Results indicate that pre-strain severely deteriorated the hot ductility of the Nb-microalloyed 09MnNiDR cryogenic steel,which was mainly attributed to precipitation of grain boundary niobium carbonitride(10-100nm).