Abstract:The erosion of surface pipelines induced by proppant flowback during shale gas production is significant. The surface pipelines in a shale gas field in the Sichuan Basin experienced perforation failures after only five months of service. To investigate the erosion features of L360N, coatings, and ceramics and optimize the selection of two protective materials, a gas–solid two-phase flow jet erosion experimental device was used to explore the erosion resistance of L360N, coatings, and ceramics under different impact velocities (15 m/s, 20 m/s, and 30 m/s). An energy dispersive spectroscope, a scanning electron microscope, and a laser confocal microscope were employed to analyze erosion morphologies. With the increase in flow velocity, the erosion depth and erosion rate of L360N, coating, and ceramic increased and peaked under an impact velocity of 30 m/s. The maximum erosion rate and maximum erosion depth of L360N were, respectively, 0.0350 mg/g and 37.5365 μm. Its primary material removal mechanism was the plowing of solid particles, and microcracks were distributed on the material surface under high flow velocities. The maximum erosion rate and maximum erosion depth of the coating were, respectively, 0.0217 mg/g and 18.9964 μm. The detachment of matrix caused by plowing is the main material removal mechanism. The maximum erosion rate and maximum erosion depth of ceramics were, respectively, 0.0108 mg/g and 12.4856 μm. The erosion mechanisms were micro-cutting and plowing. Under different particle impact velocities, different erosion morphologies were observed, but the primary erosion mechanism was the same. The erosion resistance of the ceramics was higher than that of the coatings. Therefore, ceramic lining materials could be used to protect the easily eroded parts, such as pipeline bends and tees, and reduce the failure rate by more than 93%. The study provided the data and theoretical basis for the theoretical study on oil and gas pipeline erosion and pipeline material selection.

Experimental Study on Erosion of P110 Steel in Liquid-solid Two-phase Flow

Study of the Erosion-Corrosion Behavior of P110, N80 and VM140 Steel in 3.5wt.%NaCl Solutions with Sand

Experimental study on erosion wear behavior of PFA coated stainless steel tube

Experimental Research on Erosion of P110 Tubing During Perforating

Erosion behavior of P110 tubing steel during fracturing operation

Experimental and Numerical Study on the Impact of Sand-Carrying Liquid Erosion on Coiled Tubing Wall

Research on the solid particle erosion wear of pipe steel for hydraulic fracturing based on experiments and numerical simulations

Experimental and numerical study of erosion in a non-Newtonian hydraulic fracturing fluid

Numerical Simulation on the Erosion Characteristics of Dense Particles in the Annular Channel of Downhole Fracture Pipe

Flow Velocity and Sand Loading Effect on Erosion–Corrosion during Liquid-Solid Impingement on Mild Steel

Erosion prediction model for super 13Cr tubing during large-scale hydraulic fracturing

Experimental Study on Particle Erosion Failure of Abrupt Pipe Contraction in Hydraulic Fracturing

Influence of Sand Fines Transport Velocity on Erosion-Corrosion Phenomena of Carbon Steel 90-Degree Elbow

Influence of Elbow Angle on Erosion-Corrosion of 1018 Steel for Gas–Liquid–Solid Three Phase Flow

Research on the Erosion Law and Protective Measures of L360N Steel for Surface Pipelines Used in Shale Gas Extraction

Corrosion-Wear Behavior of Well Tube Steel N80 in Sand/Output Liquid Medium from Changqing Oil Field

Erosion Resistance of Casing with Resin and Metallic Coatings in Liquid–Solid Two-Phase Flow

Slurry erosion behaviors of P110 steel and chromizing coating in liquid-solid two-phase flow

Research on the Erosion Resistance of High-Pressure Liquid–Solid Two-Phase Flow Junction Drilling Spool

Experimental and numerical simulation of erosion-corrosion of 90° steel elbow in shale gas pipeline

Erosion–corrosion behavior of X65 carbon steel in oilfield formation water