Influence of Alloying Elements on Electrochemical Behavior of Mg-Hg-Ga Anodes

Chaoqun Peng

2011-01-01

Abstract:The effects of alloying elements Hg and Ga on the electrochemical corrosion behavior of Mg anodes were studied by galvanostatic tests,hydrogen evolution tests and electrochemical impedance spectra(EIS) measurements under different polarization conditions.Scanning electron microscopy(SEM) and X-ray diffractometry(XRD) were employed to detect the microstructure and phase relationship of the above alloys.Attention was paid to the combined effect of Hg and Ga on electrochemical properties and microstructures.The results show that Mg5Ga2 and Mg21Ga5Hg3 phases precipitated along the grain boundaries in cast Mg-4.8%Hg-8%Ga alloy.Mg21Ga5Hg3 phases precipitated in cast Mg-8.8%Hg-8%Ga and Mg-7.2%Hg-8%Ga alloys.Mg3Hg and Mg21Ga5Hg3 phases precipitated in cast Mg-7.2%Hg-2.6%Ga alloy.The sequential order of the hydrogen evolution corrosion rates from small to large is Mg-7.2%Hg-2.6%Ga alloy,Mg-4.8%Hg-8%Ga alloy,Mg-7.2%Hg-8%Ga alloy,and Mg-8.8%Hg-8%Ga alloy.The smallest hydrogen evolution corrosion rate is 1.75 ml/(cm2·min).The sequential order of the electrochemical activity from large to small is Mg-8.8%Hg-8%Ga alloy,Mg-7.2%Hg-8%Ga alloy,Mg-4.8%Hg-8%Ga alloy,and Mg-7.2%Hg-2.6%Ga alloy.The most negative stable potential of-1.932 V occurs in the Mg-8.8%Hg-8%Ga alloy in the galvanostatic test with 200 mA/cm2 current density.