The role of Ga in the microstructure, corrosion behavior and mechanical properties of as-extruded Mg–5Sn–xGa alloys

Xuejian Wang,Zongning Chen,Enyu Guo,Xueqin Liu,Huijun Kang,Tongmin Wang
DOI: https://doi.org/10.1016/j.jallcom.2021.158762
IF: 6.2
2021-05-01
Journal of Alloys and Compounds
Abstract:<p>The effect of Ga element on microstructure, corrosion behavior and tensile mechanical properties of as-extruded Mg–5Sn–<em>x</em>Ga (<em>x</em> = 0, 1, 2, 3, all in wt%) alloys was investigated using immersion test, electrochemical test and tensile test. The results show that the Mg<sub>2</sub>Sn and Mg<sub>5</sub>Ga<sub>2</sub> particles are dynamically precipitated during extrusion process, and the volume fraction of Mg<sub>5</sub>Ga<sub>2</sub> precipitates increases with increasing Ga content. The corrosion resistance of Mg–5Sn alloy in the immersion test is increased approximately by four times after adding 2 wt% Ga, due to the fact that the Ga element weakens the cathodic reaction, and more stable corrosion products are formed in the Ga-containing alloys in the inner corrosion layer. The tensile strength of investigated alloys is improved monotonously with increasing Ga content. The maximum elongation to fracture reaches up to 21.7% for Mg–5Sn–1Ga alloy due to the modified basal grain texture.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
This paper aims to solve two main problems faced by magnesium - tin alloys (Mg - Sn alloys) in practical industrial applications: relatively low absolute strength and poor corrosion resistance. Specifically, the author studied the effects of adding different contents of gallium (Ga) elements on the microstructure, corrosion - resistant behavior and mechanical properties of extruded Mg - 5Sn - xGa alloys. The following are the specific problems that the paper attempts to solve: 1. **Improving mechanical properties**: - Although Mg - Sn - based alloys have good thermal stability and workability, their absolute strength is relatively low and their ductility is poor. Therefore, alloying methods are required to improve the mechanical properties of these alloys. - By adding Ga elements, it was found that with the increase of Ga content, the tensile strength and yield strength of the alloy increase monotonically. In particular, when the Ga content is 3 wt%, the tensile strength and yield strength of the Mg - 5Sn - 3Ga alloy reach 310 MPa and 250 MPa respectively, which are about 55 MPa and 76 MPa higher than those of the Mg - 5Sn alloy. 2. **Improving corrosion - resistant performance**: - Mg - Sn alloys perform poorly in corrosive environments, especially in solutions containing chloride ions, and are prone to local corrosion, resulting in a shortened service life. - After adding Ga elements, especially in the case of 2 wt% Ga, the corrosion - resistant performance of the alloy is significantly improved. Research shows that Ga elements can weaken the cathodic reaction and form a more stable corrosion product layer on the alloy surface, thereby effectively inhibiting the corrosion process. For example, the average corrosion rate of the Mg - 5Sn - 2Ga alloy is reduced from 7.01 mm/y of the Mg - 5Sn alloy to 1.69 mm/y. 3. **Comprehensive optimization**: - Through reasonable alloying design, simultaneously improve the mechanical properties and corrosion - resistant performance of Mg - Sn alloys to meet the lightweight requirements in aerospace, automotive and other fields. - Research shows that an appropriate amount of Ga elements (such as 2 wt%) can significantly improve the corrosion - resistant performance of the alloy without sacrificing mechanical properties, achieving synergistic optimization of the two. In conclusion, through systematic research, this paper reveals the action mechanism of Ga elements in Mg - Sn alloys, providing important theoretical basis and technical support for the development of high - performance magnesium alloys.