Comparative investigation on feasible hydrolysis H 2 production behavior of commercial Mg‐M (M = Ni, Ce, and La) binary alloys modified by high‐energy ball milling—Feasible modification strategy for Mg‐based hydrogen producing alloys
Xiaojiang Hou,Hongchang Shi,Lu Yang,Lei Feng,Guoquan Suo,Xiaohui Ye,Li Zhang,Yanling Yang
DOI: https://doi.org/10.1002/er.5843
IF: 4.6
2020-08-27
International Journal of Energy Research
Abstract:<p>The bulk Mg‐M (M = Nickel [Ni], cerium [Ce], and Lanthanum [La]) alloys are successfully ameliorated by high‐energy ball milling (HEBM) to modify the hydrolysis H<sub>2</sub> generation performance in simulated seawater solution (3.5 wt% NaCl). The H<sub>2</sub> generation kinetics, rate‐limiting steps, thermodynamics and the hydrolysis mechanism are investigated by combining the fitting results of the hydrolysis curves and microstructures information. The results indicate that the as‐cast Mg25Ni possesses higher generation capacity and faster initial rate. The capacities of as‐cast Mg25Ni, Mg30Ce, and Mg30La alloys at 48°C within 180 minutes are 760 mL g<sup>−1</sup>, 725 mL g<sup>−1</sup>, and 525 mL g<sup>−1</sup>. The hydrolysis H<sub>2</sub> generation apparent activation energies of the as‐cast Mg25Ni, Mg30Ce, and Mg30La alloys are 30.92, 17.05, and 28.04 kJ·mol<sup>−1</sup>, respectively. The HEBM technique can elevate the hydrolysis performance of Mg‐M alloys. And the highest H<sub>2</sub> producing capacity as high as 589 mL g<sup>−1</sup> is obtained by HEBM Mg30La alloy at 48°C within 30 minutes. The hydrolysis apparent activation energies <i>E</i><sub><i>a</i></sub> are 9.57, 14.65, and 23.88 kJ/mol for HEBM Mg25Ni, Mg30Ce, and Mg30La alloys. The initial rate and the final yield of H<sub>2</sub> generation for Mg‐based alloys are affected by the activity of matrix alloy, microstructure, particle size, surface state, and many other factors.</p>
energy & fuels,nuclear science & technology