Abstract:Redox flow batteries based on sodium polysulfide (Na 2 Sx) show promise due to sodium's high solubility in organic solvents (e.g., diglyme. However, when x is lower than 5, sodium polysulfide exhibits low solubility (less than 0.1 molal), limiting the nominal capacity of this redox-active material. Sodium phosphorothioate complexes, Na 2 P 2 Sx, have been reported as an alternative to Na2Sx. Incorporating phosphorus into the polysulfide structure improves their solubility in organic solvents, specifically in diglyme. This presentation will describe the synthesis and characterization of sodium phosphorothioate complexes (Na 2 P 2 S x , where x = 6, 7, 8, and 9) for nonaqueous redox flow batteries. The structure of these materials is explored using 31 P NMR and 23 Na NMR spectroscopy, Raman spectroscopy, and X-ray diffraction analysis. Overall, 31 P NMR results indicate that P 5+ is tetrahedrally coordinated in all structures and that Na-P-S compounds have a common PS 3 - moiety. Ongoing efforts are aimed at providing more precise assignments to the 31 P bands and correlating these findings with complementary structural information obtained from 23 Na NMR and Raman spectroscopy. Electrochemical properties of sodium polysulfide and sodium thiophosphate catholytes, specifically Na 2 S 8 and Na 2 P 2 S 8 , were also compared using CV. The voltammogram of Na 2 S 8 revealed two clear redox reactions in the 1.5-3 V range vs. Na/Na + due to a multi-step electron transfer process involving the S 2- /S 0 redox center. In contrast, Na 2 P 2 S 8 exhibited a larger peak separation (~2 V) and lower peak currents at a given scan rate, potentially indicating a significant activation barrier associated with the rearrangement of the thiophosphate’s polyanionic structure during reduction/oxidation. Despite the substantial voltage hysteresis, Na 2 P 2 S 8 displayed stable cycling performance, with a slight increase in peak current after 100 cycles. This behavior is consistent with measurements on RFBs containing a Na 2 P 2 S x catholyte, where an electrode activation process increased the cell’s reversible capacity, likely due to subtle changes in the electrode’s surface chemistry during repeated oxidation/reduction. Finally, preliminary flow cell measurements on Na 2 P 2 S 7 catholyte show reversible voltage profiles after the formation step with deep discharge. Overall, this presentation demonstrates that Na-P-S catholytes represent a promising material for high energy, low-cost redox flow batteries. Acknowledgements This research was conducted at Oak Ridge National Laboratory, managed by UT Battelle, LLC, for the U.S. Department of Energy (DOE) and is sponsored by the U.S. Department of Energy through the Energy Storage Program in the Office of Electricity.

Research Progress in Sodium Polysulfide/bromine Redox Flow Battery

Improved Formulation and Optimization of Sodium Polysulfide/Bromine Electrolytes for Redox Flow Battery

A Stable and Energy-Dense Polysulfide/Permanganate Flow Battery

The latest advances in the critical factors (positive electrode, electrolytes, separators) for sodium-sulfur battery

Recent Progress in Redox Flow Battery Research and Development

Enhancing Voltage Output in Polyanion‐Type Cathode Materials for Sodium Ion Batteries

High-Performance Li-S Batteries Boosted by Redox Mediators: A Review and Prospects

Progress and Prospects of Transition Metal Sulfides for Sodium Storage

Polymeric Active Materials for Redox Flow Battery Application

Sodium Polysulfides As Catholytes for Redox Flow Batteries

Recent Progress in Li-S and Li-Se Batteries

Low‐Cost Polyanion‐Type Sulfate Cathode for Sodium‐Ion Battery

Recent development of electrode materials in semi-solid lithium redox flow batteries

Recent developments in carbon‐based electrodes surface modification for zinc bromine flow battery

Sulfide Electrolytes for All-Solid-state Sodium Batteries: Fundamentals and Modification Strategies

Designing Advanced Polymeric Binders for High‐Performance Rechargeable Sodium Batteries

Successive ionic layer adsorption and reaction–deposited copper sulfide electrocatalyst for high-power polysulfide-based aqueous flow batteries

Electrolytes and Electrolyte/Electrode Interfaces in Sodium‐Ion Batteries: From Scientific Research to Practical Application

All-polymer Particulate Slurry Batteries.

Recent Progress in Rechargeable Sodium Metal Batteries: A Review

Advances in Vanadium-Redoxed Polyanions for High-Voltage Sodium-Ion Batteries