Homogeneous Microstructure of Bulk K4169 Superalloy Obtained by Stable Undercooling

Zhang Keren,Xie Faqin,Hu Rui,Li Jinshan,Wu Xiangqing

DOI: https://doi.org/10.1016/s1875-5372(16)30055-8

2016-01-01

Rare Metal Materials and Engineering

Abstract:By improving the method of B2O3 glass purification combined with cycle superheating based on traditional undercooling method, a stable undercooling above 200 K of 100 g bulk K4169 superalloy was obtained, and the largest undercooling went to 271 K. The effects of purification and superheating temperature on undercooling have been discussed. Moreover, the three-dimensional numerical analysis of temperature field inside the undercooled melt has been presented, and the maximum temperature deviation in different parts is only 14 K before nucleation. In contrast with the as-solidified microstructure, the grain size will increase with the increment of nucleating temperature. Generally, the difference of microstructure in 100 g undercooled K4169 superalloy is tiny and the average grain size of the superalloy with 271 K undercooling is 12±2 μm.