SOLIDIFICATION BEHAVIOR AND MICROSTRUCTURE EVOLUTION OF Fe83B17 EUTECTIC ALLOY UNDER HYPER-UNDERCOOLING

CL Yang,GC Yang,YP Lu,JQ Chen,YH Zhou
DOI: https://doi.org/10.3321/j.issn:0412-1961.2005.10.009
IF: 1.797
2005-01-01
ACTA METALLURGICA SINICA
Abstract:The solidification behavior of bulk hyper-undercooled Fe83B17 eutectic alloy has been investigated by employing molten glass slag purification incorporated with cyclical superheating techniques. It has been found that the microstructures vary with undercooling. When undercooling comes to theoretical critical hyper-undercooling 300 K, the solidification microstructure consists of alpha-Fe and Fe2B, whereas hyper-undercooling exceeds critical value 386 K, grains are more coarse and the microstructure becomes complete anomalous eutectic, Fe2B phase disappears, and the metastable phase Fe3B occurs in the roomtemperature microstructure which is a production of crystal nucleation in alloy melt. A maximum hyper-undercooling of 460 K and the metastable structure are obtained. The reason of microstructure evolution is also discussed.
What problem does this paper attempt to address?