Abstract:The influence of different annealing atmospheres (vacuum, air, reductive) on the luminescent properties of lead tungstate single crystals (PWO) has been investigated. UV-excited emission spectra and their excitation spectra of the same PWO sample at different annealing conditions were reported. The emission of PWO as grown was weak and dominated by the defect-related red band which is a disadvantage for the scintillation of PWO. The intrinsic blue band was just discernable from the red band. After air annealing, the luminescence intensity was increased enormously and the green band was turn into the prominence of the emission spectra. It suggested that the green emission originate from some local excess oxygen defects, such as (WO_4~(2-)+Oi) centers (here Oi means interstitial oxygen atom). After subsequently vacuum annealing, the emission intensity was dropped again, and the increase of 420nm excitation in the excitation spectra of the red band emission was remarkable. The color center around 420nm is harmful to the radiation hardness of PWO and should be avoid. It suggested all the unfavorable factor after vacuum annealing is caused by the increase of the concentration of oxygen vacancy Vo since the oxygen in the lattice can diffuse outward through the surface when annealing in vacuum under high temperature. So air annealing which decrease the concentration of Vo is a good method to improve the luminescence properties in full scale.In addition, the splitting of 310nm excitation band into two sharp excitation peaks around 305nm and 320nm was observed for the first time when another PWO sample was investigated after vacuum annealing. With the increasing of Vo concentration, 305nm peak lowered while 320nm peak heightened. It suggested that 305nm excitation is corresponding to the excitation of intrinsic excitons while 320nm excitation is corresponding to the bound exciton related to Vo-defects.

Influence of Sb on the Scintillation Properties of Lead Tungstate Crystal

Influence of Sb Doping on the Luminescent Properties of PbWO4 Single Crystals

Study on Radiation Damage of Lead Tungstate Crystals

Study of Scintillating Luminescence Spectra of Lead Tungstate Scintillation Crystal Doped with Ions

Study on PbWO4 doped with Y, Sb

The Influences of Monovalent Ions on the Stability of Scintillation Properties and Radiation Hardness of PbWO4:Y3+ Crystals

Antimony(III)-Doped PbWO<sub>4</sub>Crystals with Enhanced Photoluminescence via a Shape-Controlled Sonochemical Route

The Optical Properties of Scintillation PbWO4 Crystal Doped with BaF2

Bright Luminescence of Sb Doping in All-Inorganic Zinc Halide Perovskite Variant

Enhanced Electrical Conductivity and Photoconductive Properties of Sn-doped Sb2Se3 Crystals

The Study of Light Yield Increase after Low Dose Rate Irradiation in Y3+ Doping PbWO4 Crystals

Measurements of Scintillation Characteristics of Pbwo4 Crystals

Enhanced photoluminescence of Tb3+ in SnO2 film by phosphorus diffusion process

The Origin of Radiation Instability in Yttrium-Ion-Doped Lead Tungstate Crystals

Influence of Different Annealing Atmosphere on the Luminescence of PbWO4 Single Crystal

The green emission and local structure of the scintillator PbWO4

EXAFS Study on the Lanthanum Ion Doped PbWO4 Crystal

Improvement of Luminescent Properties of Pbwo4 by Doping with Gd3+ Ions

Effects of surface structure and Ag-Sb nanodots on electronic properties of PbTe (1 0 0) facets from first-principles calculations

Influence of Molar Ratio of Sb/Zn on the Crystal, Electrical and Optical Properties of Sb-doped ZnO Films

Loss of Light Yield of Doped Lead Tungstate Crystals after Irradiation