Abstract:The influence of different annealing atmospheres (vacuum, air, reductive) on the luminescent properties of lead tungstate single crystals (PWO) has been investigated. UV-excited emission spectra and their excitation spectra of the same PWO sample at different annealing conditions were reported. The emission of PWO as grown was weak and dominated by the defect-related red band which is a disadvantage for the scintillation of PWO. The intrinsic blue band was just discernable from the red band. After air annealing, the luminescence intensity was increased enormously and the green band was turn into the prominence of the emission spectra. It suggested that the green emission originate from some local excess oxygen defects, such as (WO_4~(2-)+Oi) centers (here Oi means interstitial oxygen atom). After subsequently vacuum annealing, the emission intensity was dropped again, and the increase of 420nm excitation in the excitation spectra of the red band emission was remarkable. The color center around 420nm is harmful to the radiation hardness of PWO and should be avoid. It suggested all the unfavorable factor after vacuum annealing is caused by the increase of the concentration of oxygen vacancy Vo since the oxygen in the lattice can diffuse outward through the surface when annealing in vacuum under high temperature. So air annealing which decrease the concentration of Vo is a good method to improve the luminescence properties in full scale.In addition, the splitting of 310nm excitation band into two sharp excitation peaks around 305nm and 320nm was observed for the first time when another PWO sample was investigated after vacuum annealing. With the increasing of Vo concentration, 305nm peak lowered while 320nm peak heightened. It suggested that 305nm excitation is corresponding to the excitation of intrinsic excitons while 320nm excitation is corresponding to the bound exciton related to Vo-defects.

The green emission and local structure of the scintillator PbWO4

Study on Radiation Damage of Lead Tungstate Crystals

First‐principles Study of PbWO4 Crystal with Interstitial Oxygen Atoms

Influence of Different Annealing Atmosphere on the Luminescence of PbWO4 Single Crystal

Influence of Sb Doping on the Luminescent Properties of PbWO4 Single Crystals

Measurements of Scintillation Characteristics of Pbwo4 Crystals

Influence of Sb on the Scintillation Properties of Lead Tungstate Crystal

Photoinduced oxygen-vacancy related centers in PbWO 4 : Electron spin resonance and thermally stimulated luminescence study

EXAFS Study on the Lanthanum Ion Doped PbWO4 Crystal

Excitation Dependent Phosphorous Property and New Model of the Structured Green Luminescence in ZnO

Revealing the Competition Between Defect‐Trapped Exciton and Band‐Edge Exciton Photoluminescence in Monolayer Hexagonal WS2

The Optical Properties of Scintillation PbWO4 Crystal Doped with BaF2

Study of Scintillating Luminescence Spectra of Lead Tungstate Scintillation Crystal Doped with Ions

Antimony(III)-Doped PbWO<sub>4</sub>Crystals with Enhanced Photoluminescence via a Shape-Controlled Sonochemical Route

Structure and Upconversion Luminescence of Hydrothermal PbWO4:Er3+, Yb3+Powders

Characterization of a defective PbWO4 crystal cut along the a-c crystallographic plane: structural assessment and a novel photoelastic stress analysis

Improvement of Luminescent Properties of Pbwo4 by Doping with Gd3+ Ions

Resonant Nature of Intrinsic Defect Energy Levels in Pbte Revealed by Infrared Photoreflectance Spectroscopy

SONOCHEMICAL SYNTHESIS OF PbWO4 NANOPARTICLES

Study on PbWO4 doped with Y, Sb

ESR and TSL study of hole capture in PbWO_4:Mo,La and PbWO_4:Mo,Y scintillator crystals