Abstract:In this study, Fe, one of the inexpensive beta-phase stabilizers, was employed to fabricate Ti alloys by the powder metallurgy route. The formation mechanism of unique microstructures and texture of the extruded Ti-Fe alloy was elucidated through scanning electron microscopy-electron backscatter diffraction (SEM-EBSD) and transmission electron microscopy-energy-dispersive X-ray spectroscopy (TEM-EDS). For the Ti-Fe alloys consolidated from the pre-mixed pure Ti powder and Fe particles by spark plasma sintering and following hot extrusion, the additive Fe atoms existed as solid solution atoms in beta-Ti phase. The increment in the Fe content was effective in increasing the beta-Ti phase volume fraction and refining the alpha-Ti grains. The mean alpha-Ti grain size of Ti-4 wt.% Fe alloy was 1.27 mu m, which was about ten times less than that of the pure Ti material (12.42 mu m). The alpha and beta phases of the extruded Ti-1-4 wt.% Fe material were aligned in parallel to the extrusion direction, and they suppressed the grain growth of each other. Although yield stress (YS) and tensile strength (TS) remarkably increased to 1093 MPa and 1183 MPa, respectively, with an increase in the Fe content, a large elongation of 28-38% was obtained in the extruded Ti-Fe alloys. These tensile properties were favorable compared to the commercial Ti-6 wt.% Al-4 wt.% V alloy. The dominant strengthening factors for the Ti-Fe alloys were alpha-Ti grain refinement and beta-Ti hard phase dispersion. In the case of 4 wt% Fe addition, 50% of the YS increment was due to the latter strengthening mechanism.

Effect of Fe Content on Microstructures and Properties of Ti6Al4V Alloy with Combinatorial Approach

Effect Of Fe Content On The As-Cast Microstructures Of Ti-6al-4v-Xfe Alloys

Effect of Fe content on microstructure and hardness of Ti-4.5Mo–5Al-1.8Zr-2.5Cr-1.1Sn titanium alloy based on high-throughput diffusion couple

Effect of Fe Content on Microstructure Evolution and Mechanical Properties of as-cast Ti-xFe-B Alloy

Investigation of the Influence of Cr on the Microstructure and Properties of Ti6Al4VxCr Alloys with a Combinatorial Approach

Investigation of the Influence of Fe on the Microstructure and Properties of Ti5553 Near-Β Titanium Alloy with Combinatorial Approach

Effect of Ti on Microstructure and Mechanical Properties of Die-Cast Al-Mg-Zn-Si Alloy

Effects of Fe Contents on the Microstructure and Precipitate of Ti–Al–V Alloys Prepared by Direct Energy Deposition

Influence of Ti addition on microstructure and mechanical behavior of a FCC-based Fe30Ni30Co30Mn10 alloy

Precipitation Response and Hardening Behaviors of Fe-modified Ti5553 Alloy

Fe Element Promotes the Transformation from Columnar to Equiaxed Grains and the Formation of Ultrafine Microstructure of Ti-6Al-4V Alloy by Laser Wire Deposition

Microstructure Evolution and Grain Refinement Behavior During Hot Deformation of Fe Micro-Alloyed Ti-6Al-4V

Improvement of microstructure and mechanical properties of TiAl?Nb alloy by adding Fe element

Effect of Α Composite Layer on the Microstructure and Mechanical Properties of Ti-10V-2Fe-3Al Alloy

Effect of Ti content on microstructures and mechanical properties of cast Al-2Li-2Cu-0.5Mg alloy

Optimal Design of High-Strength Ti‒Al‒V‒Zr Alloys Through a Combinatorial Approach

Compositional and Microstructural Optimization and Mechanical-Property Enhancement of Cast Ti Alloys Based on Ti-6Al-4V Alloy

Microstructure and tensile properties of a multi-alloyed α + β titanium alloy Ti4.5Al10.5V3Fe

Microstructures Analysis and Quantitative Strengthening Evaluation of Powder Metallurgy Ti–Fe Binary Extruded Alloys with (Α+β)-Dual-phase

Effect of heat treatment on microstructure and mechanical property of Ti-6Al-2.5V-1.5Fe-0.15O alloy

Microstructure and mechanical properties of powder metallurgy Ti-TiBw-xFe titanium matrix composites using Ti-TiBw composite powder