Abstract:A newly designed Fe-Cr-Mn alloy, considered as a candidate intermediate-temperature solid oxide fuel cell ( SOFC) interconnect material, was cyclically oxidized at 650 degrees C, 750 degrees C, and 850 degrees C in a reducing atmosphere consisting of N-2+3.75 vol% H-2+25 vol% H2O( g) and corresponding to the SOFC anode environment. Results indicate that this alloy possesses good oxidation resistance and acceptable electrical conductivity at 750 degrees C in the reducing atmosphere. During the 1000 h oxidation, the oxide scale formed on the substrate at this temperature consists of an inner layer of Cr2O3 doped with Ti, a Mn-rich middle layer of Mn-Cr spinel and Mn2TiO4, and a top layer of MnO, with an overall thickness of around 3 mu m. The oxidation kinetics at 750 degrees C obey a parabolic law with rate constants of 1.37 x 10(-13) g(2) cm(4) s(-1) from 0 to 130 h, and of 8.84 x 10(-14) g(2) cm(-4) s(-1) from 130 to 1000 h. The area specific resistance (ASR) of the oxide scale measured at 750 degrees C is 16.3m Omega cm(2), which is higher than that formed in the oxidizing atmosphere but is still within the maximum limit of 100m Omega cm(2), required for metallic interconnects. The increase in oxidizing temperature from 650 degrees C to 850 degrees C promoted the outward diffusion of Mn and Ti ions, thus changing the composition and morphology of the formed oxides; in addition, the oxidation rate of the alloy increased dramatically, leading to an increase of both the oxide scale thickness and the ASR values. (C) 2018 Elsevier B.V. All rights reserved.

Porous Nickel-Iron Alloys As Anode Support for Intermediate Temperature Solid Oxide Fuel Cells: II. Cell Performance and Stability

Porous Ni–Fe Alloys As Anode Support for Intermediate Temperature Solid Oxide Fuel Cells: I. Fabrication, Redox and Thermal Behaviors

Oxidation behavior of a Ni-Fe support in SOFC anode atmosphere

A Novel High Performance Composite Anode with in Situ Growth of Fe-Ni Alloy Nanoparticles for Intermediate Solid Oxide Fuel Cells

A Robust Carbon Tolerant Anode for Solid Oxide Fuel Cells

High performance Ni–Fe alloy supported SOFCs fabricated by low cost tape casting-screen printing-cofiring process

Effect of Anode Calcination on the Performance and Redox Stability of Low-Temperature Solid Oxide Fuel Cells Prepared Via Impregnation

Fabrication and Study on Ni1−xFexO-YSZ Anodes for Intermediate Temperature Anode-Supported Solid Oxide Fuel Cells

A Rational Design of FeNi Alloy Nanoparticles and Carbonate-Decorated Perovskite As a Highly Active and Coke-Resistant Anode for Solid Oxide Fuel Cells

A Redox-Robust Ceramic Anode-Supported Low-Temperature Solid Oxide Fuel Cell

Electrochemical performance and redox stability of solid oxide fuel cells supported on dual-layered anodes of Ni-YSZ cermet and Ni–Fe alloy

Effects of Adding Alumina to the Nickel-Zirconia Anode Materials for Solid Oxide Fuel Cells and a Two-Step Sintering Method for Half-Cells

Fabrication of Metal-Supported Tubular Solid Oxide Fuel Cell by Phase-Inversion Method and in Situ Reduction

Performance Evaluation of a New Fe-Cr-Mn Alloy in the Reducing Atmosphere of Solid Oxide Fuel Cells

Electrochemical Property of Multi-Layer Anode Supported Solid Oxide Fuel Cell Fabricated Through Sequential Tape-Casting and Co-Firing

Oxidation Behavior and Electrical Property of A Ni-Based Alloy in Sofc Anode Environment

Improved Microstructure and Performance of Ni-based Anode for Intermediate Temperature Solid Oxide Fuel Cells

High-Performance Low-Temperature Solid Oxide Fuel Cell with a Pt@C–Ni 0.8 Co 0.15 Al 0.05 LiO 2−δ Composite Cathode

Methane On-Cell Reforming in Nickel–iron Alloy Supported Solid Oxide Fuel Cells

Performance and Optimization of Ni/3 Mol% Y2O3-ZrO2 Anode Supported SOFC

High-performance Ni In-Situ Exsolved Ba(Ce0.9Y0.1)0.8Ni0.2O3-δ/Gd0.1Ce0.9O1.95 Composite Anode for SOFC with Long-Term Stability in Methane Fuel