Abstract:The reduction behavior of a sintered NiO/YSZ anode used for intermediate temperature solid oxide fuel cells was studied by hydrogen temperature-programmed reduction (H-2-TPR). The reduction process of the NiO/YSZ anode in the cell was in situ monitored by open circuit voltage (OCV) and electrochemical impedance spectroscopy (EIS). H-2-TPR results show that the higher sintering temperature of the NiO/YSZ anode results in a slower reduction of NiO to metallic Ni. However, when the sintering temperature is elevated to 1500 degrees C, the reduction of sintered NiO/YSZ anode powder instead becomes easier. The higher NiO content in the anode leads to the more rapid reduction of the corresponding anode powder. The above H2-TPR results can be attributed to the combined effects of the growth up of NiO particles and the interface separation between NiO and YSZ caused by the anode sintering. The variation of OCVs reveals that for the cells, the anode with higher NiO content has a slower reduction process, which can be ascribed to the retarding effect of excessive H2O produced during the initial reduction period. It was found from the EIS results that the 50% NiO/YSZ anode has a most stable reduction process, whereas for the cells with 30 % and 70 % NiO/YSZ anodes, both the polarization resistances gradually increase after experiencing an initial decrease for a short period. The cell polarization resistance with 30 % NiO/YSZ anode keeps no change any more after reduction for 600 min, whereas the cell polarization resistance with 70 % NiO/YSZ anode increases continuously.

Improved Microstructure and Performance of Ni-based Anode for Intermediate Temperature Solid Oxide Fuel Cells

Evaluation of Ni and Ni–Ce0.8Sm0.2O2−δ (SDC) Impregnated 430L Anodes for Metal-Supported Solid Oxide Fuel Cells

Porous Ni–Fe Alloys As Anode Support for Intermediate Temperature Solid Oxide Fuel Cells: I. Fabrication, Redox and Thermal Behaviors

The Reduction Process of a NiO/YSZ Anode for Intermediate Temperature Solid Oxide Fuel Cells

Nano-Structured Anodes of Solid Oxide Fuel Cells

Ni-Sm2o3 Cermet Anodes for Intermediate-Temperature Solid Oxide Fuel Cells with Stabilized Zirconia Electrolytes

Achieve a high electrochemical oxidation activity by a self-assembled cermet composite anode with low Ni content for solid oxide fuel cells

Effects of Initial Reduction Temperature on the Microstructures and Performances of Ni/YSZ Anodes for Solid Oxide Fuel Cells

Effect of Impregnation Phases on the Performance of Ni-based Anodes for Low Temperature Solid Oxide Fuel Cells

Preparation and Electrochemical Performance of Silver Impregnated Ni-YSZ Anode for Solid Oxide Fuel Cell in Dry Methane

Fabrication and Study on Ni1−xFexO-YSZ Anodes for Intermediate Temperature Anode-Supported Solid Oxide Fuel Cells

Microstructure Modification of Nio/Ysz Anode in Solid Oxide Fuel Cell by Particle Size Gradation of Ysz

Microstructure Tailoring of the Nickel Oxide-Yttria-Stabilized Zirconia Hollow Fibers Toward High-Performance Microtubular Solid Oxide Fuel Cells

Ni/YSZ and Ni–CeO2/YSZ Anodes Prepared by Impregnation for Solid Oxide Fuel Cells

Impregnated Nickel Anodes for Reduced-Temperature Solid Oxide Fuel Cells Based on Thin Electrolytes of Doped LaGaO3

Fabrication and Evaluation of NiO/Y2O3-stabilized-ZrO2 Hollow Fibers for Anode-Supported Micro-Tubular Solid Oxide Fuel Cells

A Novel Method to Purposely Modify the Anode/Electrolyte Interface in Solid Oxide Fuel Cells

Enhanced Performance of Solid Oxide Fuel Cells with Ni/CeO2 Modified La0.75Sr0.25Cr0.5Mn0.5O3− Anodes

Rational Design of Superior, Coking-Resistant, Nickel-Based Anodes Through Tailoring Interfacial Reactions for Solid Oxide Fuel Cells Operated on Methane Fuel.

High Performance Ni–Sm2O3 Cermet Anodes for Intermediate-Temperature Solid Oxide Fuel Cells

Performance and Optimization of Ni/3 Mol% Y2O3-ZrO2 Anode Supported SOFC