Enhanced Performance of Solid Oxide Fuel Cells with Ni/CeO2 Modified La0.75Sr0.25Cr0.5Mn0.5O3− Anodes
Xingbao Zhu,Zhe Lue,Bo Wei,Kongfa Chen,Mingliang Liu,Xiqiang Huang,Wenhui Su
DOI: https://doi.org/10.1016/j.jpowsour.2009.01.035
IF: 9.2
2009-01-01
Journal of Power Sources
Abstract:The optimization of electrodes for solid oxide fuel cells (SOFCs) has been achieved via a wet impregnation method. Pure La0.75Sr0.25Cr0.5Mn0.5O3−δ (LSCrM) anodes are modified using Ni(NO3)2 and/or Ce(NO3)3/(Sm,Ce)(NO3)x solution. Several yttria-stabilized zirconia (YSZ) electrolyte-supported fuel cells are tested to clarify the contribution of Ni and/or CeO2 to the cell performance. For the cell using pure-LSCrM anodes, the maximum power density (Pmax) at 850°C is 198mWcm−2 when dry H2 and air are used as the fuel and oxidant, respectively. When H2 is changed to CH4, the value of Pmax is 32mWcm−2. After 8.9wt.% Ni and 5.8wt.% CeO2 are introduced into the LSCrM anode, the cell exhibits increased values of Pmax 432, 681, 948 and 1135mWcm−2 at 700, 750, 800 and 850°C, respectively, with dry H2 as fuel and air as oxidant. When O2 at 50mLmin−1 is used as the oxidant, the value of Pmax increases to 1450mWcm−2 at 850°C. When dry CH4 is used as fuel and air as oxidant, the values of Pmax reach 95, 197, 421 and 645mWcm−2 at 750, 800, 850 and 900°C, respectively. The introduction of Ni greatly improves the performance of the LSCrM anode but does not cause any carbon deposit.