Methane On-Cell Reforming in Nickel–iron Alloy Supported Solid Oxide Fuel Cells

Kai Li,Lichao Jia,Xin Wang,Jian Pu,Bo Chi,Li Jian
DOI: https://doi.org/10.1016/j.jpowsour.2015.03.062
IF: 9.2
2015-01-01
Journal of Power Sources
Abstract:Ni0.9Fe0.1-supported solid oxide fuel cells are fabricated by tape casting-screen printing-sintering process; and the activity for CH4 reforming and electrochemical performance are examined with wet (3 vol.% H2O) CH4 as the fuel at 650 degrees C, in comparison with Ni-supported cells. At a flow rate of 100 ml min(-1), the wet CH4 is partially (35 vol.%) reformed to H-2, CO and CO2 in the Ni0.9Fe0.1 anode-support, demonstrating a higher reforming activity than that of the Ni anode-support. The maximum power density is 1.01 Wcm(-2) at a high limiting current density of 2.6 A cm(-2); and cell voltage at 0.4 A cm(-2) is slightly decreased from 0.65 to 0.60 V within 50 h durability test. This high performance is attributed to the Ni0.9Fe0.1 anode-support that is more active for CH4 reforming and resistant to carbon deposition than its Ni counterpart. (C) 2015 Elsevier B.V. All rights reserved.
What problem does this paper attempt to address?