Abstract:In spite of the advantages of LiNi 0.8 Co 0.1 Mn 0.1 O 2 (NCM811) cathode materials such as high energy density and high capacity, their capacity decay during cycling is still a significant problem, which are mainly due to the internal structural collapse and the surge in interfacial impedance caused by interfacial side reactions. To address these issues, wet chemical methods and annealing treatments were used to create LiV 2 O 4 -coated and V 4+ -doped NCM811 cathode materials. The LiV 2 O 4 coating layer and the doped V 4+ had little effect on the crystal structure of the NCM811, according to X-ray powder diffraction and Rietveld refinement studies. Scanning electron microscopy, energy dispersive spectroscopy, X-ray photoelectron spectroscopy, and transmission electron microscopy data all showed that the LiV 2 O 4 layer was successfully coated on the surface of the spherical particles and some of the V 4+ was successfully introduced into the bulk phase. Thanks to the ion-conducting layer, LiV 2 O 4 , the interfacial impedance was reduced while the Li + diffusion rate was accelerated, and the V 4+ doped into the bulk phase stabilizes the internal structure, significantly increasing the cycling stability and the rate performance of NCM811. In particular, when the coating amount was 0.6 wt%, the initial discharge specific capacity reached 203.5 mAh/g at 2.8–4.3 V at 0.1 C, and the retention rate was 87.6% after 100 cycles, which was 12.1% higher compared to 75.5% of the original sample. And when the rate was raised to 5 C, the original sample's capacity plummeted to only about 100 mAh/g, but the sample with 0.6 wt% of coating was still 140.9 mAh/g. Experiments confirmed that this LiV 2 O 4 coating modification with synergistic V 4+ doping provided an innovative technique for boosting the electrochemical performance of Ni-rich ternary cathode materials.

Enhanced Electrochemical Performance of Dual-Conductive Layers Coated Ni-rich LiNi0.6Co0.2Mn0.2O2 Cathode for Li-ion Batteries at High Cut-off Voltage

Radially Oriented Single‐Crystal Primary Nanosheets Enable Ultrahigh Rate and Cycling Properties of LiNi0.8Co0.1Mn0.1O2 Cathode Material for Lithium‐Ion Batteries

Ionic Conductive Interface Boosting High Performance LiNi0.8Co0.1Mn0.1O2 for Lithium Ion Batteries

Enhanced electrochemical performance of Li 1.2 Mn 0.54 Ni 0.13 Co 0.13 O 2 cathode material coated with Li + -conductive Li 2 SiO 3 for lithium ion batteries

Improving electrochemical performance of Ni-rich LiNi0.8Co0.1Mn0.1O2 cathode for Li-ion batteries by dual-conductive coating layer of PPy and LiAlO2

Multifunctional Integration of Double-Shell Hybrid Nanostructure for Alleviating Surface Degradation of LiNi0.8Co0.1Mn0.1O2 Cathode for Advanced Lithium-Ion Batteries at High Cut-Off Voltage.

Multifunctional Integration of Double-Shell Hybrid Nanostructure for Alleviating Surface Degradation of LiNi<sub>0.8</sub>Co<sub>0.1</sub>Mn<sub>0.1</sub>O<sub>2</sub> Cathode for Advanced Lithium-Ion Batteries at High Cutoff Voltage

High structure stability and Li-conduction of LiNi0.8Co0.1Mn0.1O2 cathode co-coated by Al2O3 and LiNbO3 for high performance lithium-ion battery

Synergistic effects of conformal surface precise nanofilm coating and doping on single-crystal LiNi0.5Co0.2Mn0.3O2 at high voltage

Enhanced High-Voltage Cycling Stability of Ni-rich LiNi0.8Co0.1Mn0.1O2 Cathode Coated with Li2O–2B2O3

Double Conductor Coating to Improve the Structural Stability and Electrochemical Performance of LiNi 0.8 Co 0.1 Mn 0.1 O 2 Cathode Material

Enhanced electrochemical performance of LiV2O4-coated and V4+-doped LiNi0.8Co0.1Mn0.1O2 cathode for lithium-ion batteries

Double Conductor Coating to Improve the Structural Stability and Electrochemical Performance of LiNi0.8Co0.1Mn0.1O2 Cathode Material

Protective and ion conductive: High-Rate Ni-Rich cathode with enhanced cyclic stability via One-Step bifunctional dual-layer coating

Enhanced rate performance and mitigated capacity decay of single-crystal LiNi0.8Co0.1Mn0.1O2 by the synergism of Mg doping and V2O5 coating

Sol/Antisolvent Coating for High Initial Coulombic Efficiency and Ultra-stable Mechanical Integrity of Ni-Rich Cathode Materials

Enhanced electrochemical properties of Ni-rich LiNi0.8Co0.1Mn0.1O2 by SnO2 coating under high cutoff voltage

Understanding the Effects of Surface Modification on Improving the High-Voltage Performance of Ni-rich Cathode Materials

Mixed-conducting Interlayer Boosting the Electrochemical Performance of Ni-rich Layered Oxide Cathode Materials for Lithium Ion Batteries

Improved Rate Capability and Cycle Stability of Li[Ni 0.5 Co 0.2 Mn 0.3 ]O 2 with Li 2 MnO 3 Coating under High Cut-off Voltage

Superior Stability Secured by a Four-Phase Cathode Electrolyte Interface on a Ni-Rich Cathode for Lithium Ion Batteries