Effects of MgO/CaO ratio on the crystal phase composition and performance of MgO-CaO-B2O3-SiO2 glass–ceramics for LTCC applications
Yanyun Zhao,Junyou Chen,Yunhe Yi,Min Zhou,Jiandong Cui,Qingmeng Zhang
DOI: https://doi.org/10.1007/s10854-024-13200-4
2024-07-18
Journal of Materials Science Materials in Electronics
Abstract:The MgO-CaO-B 2 O 3 -SiO 2 (MCBS) glass–ceramics with different MgO/CaO ratio were designed and prepared. The phase transition, microstructure, dielectric properties and flexural strength of the MCBS system were investigated. The quantitative calculations results showed that the MgO/CaO ratio favored the formation of CaMgSi 2 O 6 phase but hindered the formation of CaSiO 3 and CaB 2 O 4 phases. With increasing MgO/CaO ratio, the microstructure of sample changes from dendritic to polygonal shape. The MgO/CaO ratio also affected the properties of matrix. In this study, the 5MgO-36CaO-18B 2 O 3 -41SiO 2 (mol%) sample sintered at 825 °C for 15 min exhibited superior performance: the density of 2.64 g cm −3 , a moderate dielectric constant of 5.92, the dielectric loss of 1.54 × 10 –3 (10 GHz), the thermal expansion coefficient of 9.61 ppm K −1 , the thermal conductivity of 3.02 W m −1 K −1 , and a high flexural strength of 208.7 MPa, which might be a potential material for LTCC applications.
materials science, multidisciplinary,engineering, electrical & electronic,physics, applied, condensed matter