Doping Effects of Mn 2+ on the Dielectric Properties of Glass-Doped BaTiO 3 -Based X8R Materials

Bin Tang,Shuren Zhang,Xiaohua Zhou,Ying Yuan

DOI: https://doi.org/10.1007/s10854-006-9076-5

2007-01-01

Journal of Materials Science Materials in Electronics

Abstract:In this paper, Mn2+ and calcium borosilicate glass (CBS) were used as effective dopants to prepare environmentally friendly dielectric materials satisfying EIA X8R specification. The effects of various Mn2+ concentrations on the dielectric properties of BaTiO3 (BT) ceramics were investigated when CBS amount was fixed. The dielectric measurements showed that the permittivity was decreased continuously with increasing Mn2+ concentrations, resulted from the existence of paraelectric regions caused by Mn2+ doping. The dielectric loss was decreased at the beginning and then increased with increasing Mn2+ concentrations, whereas the resistivity showed an opposite movement. The SEM images and X-ray diffraction curves corresponding to BT ceramics doped with different Mn2+ amounts proved that Mn2+ can promote the crystallization of CBS glass to form the secondary phase Ca4Mn4Si8O24, which determines the intensity of the high temperature peak (at about 125 °C) of the variation rate curve of capacitance. Moreover, the modification effects of Mn2+ on the dielectric properties of BT have been investigated. It is revealed that a proper usage of Mn2+ can improve the dielectric properties significantly, and Mn2+ and CBS co-doped BT ceramics are promising to develop X8R MLCs.