EFFECT OF Mn ION IN NANO-DOPANT ON BaTiO3-BASED DIELECTRICS FOR MULTILAYER CERAMIC CAPACITOR

LI Bo,ZHANG Shuren,ZHOUXiaohua,CHEN Zhu,JIA Chenggang

DOI: https://doi.org/10.3321/j.issn:0454-5648.2006.03.007

2006-01-01

Abstract:Nano-composite oxide dopant Y_3MgMn_xSiO_ 7.5+x (x=0.1,0.2,0.5,1.0) was synthesized by the solgel method and BaTiO_3-based ultrafine nonreducible dielectrics for multilayer ceramic capacitance were prepared by the nano-doping process. Xerogel and calcined nanopowder were characterized by thermogravimetricdifferential thermal analysis, X-ray diffraction and transmission electron microscopy. The effect of manganese ion in nano-dopant on the microstructure and dielectric properties as well as the non-reducibility of BaTiO_3-based ceramics were investigated. The results indicate that the average particle size of nanopowder Y_3MgMn_xSiO_ 7.5+x calcined at 650, 750, 850℃ and 950℃ is about 25.9, 40.2, 51.8nm and 67.9nm, respectively, and the BaTiO_3-based nanopowder begins to crystallize around 850℃. Mn can dramatically inhibit the grain growth of BaTiO_3 -based ceramics and promote the formation of fine grain structure (average grain size about 0.4μm). With the increase of Mn content in nano-dopant, the crystal structure of ceramics transform from tetragonal to pseudocubic and the coreshell structuses are perfectly formed. Accordingly, the dielectric temperature characteristics are improved and the permittivity at room temperature is more than 2600. Multivalent Mn ion in nano-dopant acting as an acceptor can effectively restrain the electronic concentration and reinforce the non-reducibility of the ceramics. Dielectric loss of the ceramic is lower than 1.0 % and insulation resistivity increases to 10 12 Ω·cm consequently. BaTiO_3-based dielectrics with high performances can be obtained to meet the requirements of EIA X7R/X8R standards.