Effect of ZrO2 Doping on Properties of BaO-B2O3-SiO2 Glass-ceramics

Bo TANG,Bo LI

DOI: https://doi.org/10.7521/j.issn.0454-5648.2013.12.09

2013-01-01

Abstract:BaO-B2O3-SiO2 glass-ceramic with high thermal expansion behavior were prepared by a solid-state method. Thermal, mechanic, electric properties of glass-ceramic composite materials and its scanning electron microscope, X-ray diffractometer and differential scanning calorimetry were used to research the effect of ZrO2 doping on the properties of BaO-B2O3-SiO2 glass-ceramic. The results show that as the ZrO2 doped content increases, microscopic, the cristobalite phase of glass-ceramic content reduced sig-nificantly, the quartz crystal phase content increased significantly;macroscopic, the bending strength and the relative permittivity of the glass-ceramic gradually increase, the thermal expansion coefficient gradually decrease slightly, the high thermal expansion coeffi-cient can be adjusted by doping ZrO2, the thermal expansion coefficient changes with temperature tend to be more linear, optimized the thermal properties of glass-ceramic. When sintering temperature is 950℃, ZrO2 doped content is 5%, BaO-B2O3-SiO2 glass ceramics were obtained with maximum bending strength (181 MPa), higher CTE (14.21 × 10-6/℃), lower relative dielectric constant (6.4) and lower dielectric loss (0.4%). This glass ceramics can meet the requirement of glass ceramics low temperature co-fired ce-ramics package materials.