Abstract:The selective catalytic reduction (SCR) technique that converts NOx from the outlet of industrial boilers at low temperature (<200 °C) requires catalysts that possess both the oxidization property of NOx and the adsorption ability to NH3. However, owing to unsuitable redox capacity, most NH3-SCR catalysts such as MnO2/TiO2 and MnO2–CeO2/TiO2 suffer from poor activity and N2 selectivity and SO2 poisoning. Benefiting from constructing mesoporous MnCeSmTiOx amorphous mixed oxides by the coprecipitation method, enhanced SO2-tolerant low-temperature NH3-SCR performance was achieved. The MnCeSmTiOx catalysts have an amorphous and mesoporous structure with a BET surface area of 214 m2·g–1. The NO conversion could reach nearly 100% at 140–320 °C and maintain >90% at 400 °C and a gas hourly space velocity of 80,000 h–1. The selectivity of N2 could be maintained at ≈100% at 100–320 °C and stay at >90% up to 400 °C. Besides, the MnCeSmTiOx catalyst preserves higher catalytic performance after introducing H2O and SO2 compared with the catalysts without adding Sm. The redox properties, acidic properties, and reaction intermediates of catalysts were analyzed by X-ray photoelectron spectroscopy, hydrogen temperature-programmed reduction, ammonia temperature-programmed desorption (NH3-TPD), O2-TPD, pyridine-IR, thermogravimetry–differential scanning calorimetry, and diffuse reflectance infrared Fourier transform. The synergistic effect of the Lewis acid sites and oxidation catalytic sites of mixed oxides serves for the conversion of NO to N2 by following the Langmuir–Hinshelwood mechanism. Doping Sm into MnCeSmTiOx can increase oxygen vacancies and transfer electrons to Mn4+ and Ce4+, which facilities the formation of active adsorbed NO2, bidentate nitrate, and bridging nitrate intermediates and suppresses SO2 poisoning by inhibiting the oxidation of SO2 by Mn4+ and Ce4+. Our work could be beneficial to modulate the redox capacity of active sites on NH3-SCR catalysts so that NOx can be eliminated in complex flue gas at low temperatures.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acscatal.0c02567?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acscatal.0c02567</a>.Experimental details, kinetic experiments and the calculation process of the reaction rate, reaction order, and TOF; XRD patterns; TEM images; and in situ DRIFTS spectra with adsorption of NH3 NO + O2 on MnSmTiOx and CeSmTiOx catalysts (<a class="ext-link" href="/doi/suppl/10.1021/acscatal.0c02567/suppl_file/cs0c02567_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Ho-modified Mn-Ce/TiO2 for low-temperature SCR of NOx with NH3: Evaluation and characterization

Investigation on the redox/acidic features of bimetallic MOF-derived CeMOx catalysts for low-temperature NH3-SCR of NOx

Influence of Ho doping on the deNOx performance of Mn-Ce/TiO2 low temperature SCR catalyst

C,N‐modified TiO2‐supported Mn–Ce–Cox‐based Catalyst for Low‐temperature NH3‐SCR

C,N ‐modified TiO 2 ‐supported Mn–Ce–Co x ‐based catalyst for low‐temperature NH 3 ‐SCR

Low-temperature selective catalytic reduction of NO with NH3 over Mn–Ce–Ox/TiO2: a comparison between catalyst preparation methods

Comparison of low-temperature catalytic activity and H2O/SO2 resistance of the Ce-Mn/TiO2 NH3-SCR catalysts prepared by the reverse co-precipitation, co-precipitation and impregnation method

Unveiling a remarkable enhancement role by designing a confined structure Ho-TNTs@Mn catalyst for low-temperature NH3-SCR reaction

Study on H2O2, Ce, W modified MnO /TiO2 based NH3-SCR Catalyst: The status and effect of doped promoters and synergies

Effect of Preferential Exposure of Anatase TiO2 {0 0 1} Facets on the Performance of Mn-Ce/TiO2 Catalysts for Low-Temperature Selective Catalytic Reduction of NOx with NH3

Low-temperature SCR of NO with NH3 over AC/C Supported Manganese-Based Monolithic Catalysts

High Resistance of SO2 and H2O over Monolithic Mn-Fe-Ce-Al-O Catalyst for Low Temperature NH3-SCR

Significant Effects of Adding Mode on Low-Temperature De-NOx Performance and SO2 Resistance of a MnCeTiOx Catalyst Prepared by the Co-Precipitation Method

Nb-modified Mn/Ce/Ti Catalyst for the Selective Catalytic Reduction of NO with NH3 at Low Temperature

Improved Activity and SO 2 Resistance by Sm-Modulated Redox of MnCeSmTiO x Mesoporous Amorphous Oxides for Low-Temperature NH 3 -SCR of NO

Effect of Nb‐doping on the MnFeOx catalyst for NH3‐SCR reaction at low‐temperature

Catalytic performance of CeO2-NPs and α-MnO2 mixed oxides catalysts for low-temperature NH3-SCR of NO

Improvement of Activity and SO2 Tolerance of Sn-Modified MnOx–CeO2 Catalysts for NH3-SCR at Low Temperatures

Sulfur/water resistance and regeneration of MnO -CeO2/TiO2 catalyst for low-temperature selective catalytic reduction of NO

Ceria modified MnOx/TiO2 as a superior catalyst for NO reduction with NH3 at low-temperature

Synthesis of novel Co(3-x)MnxO4@TiO2 core-shell catalyst for low-temperature NH3-SCR of NOx with enhanced SO2 tolerance