Thermal and mechanical properties of Sc2O3–CeO2 co-stabilized zirconia ceramic as promising thermal barrier coating material
Jinshuang Wang,Mengdi Chen,Yiyan Xu,Luyao Chen,Yongsheng Yu,Junbin Sun,Yinghui Wang,Bing Liu,Qiangshan Jing
DOI: https://doi.org/10.1016/j.ceramint.2021.08.184
IF: 5.532
2021-12-01
Ceramics International
Abstract:CeO2 and Sc2O3 co-stabilized ZrO2 ceramics have attracted much attention as potential thermal barrier coatings (TBCs) materials for applications above 1300 °C. In this study, a series of Sc0.04CexZr0.96-xO1.98 (SCZ, x = 0.08, 0.10, 0.12, 0.16) ceramic materials were synthesized with the solid-state method and their phase stability, microstructures and thermo-physical properties were systemically investigated by x-ray diffraction (XRD), Raman spectra, field emission scanning electron microscopy (SEM), thermal dilatometer, laser flash apparatus (LFA), and Vickers hardness tester. The results showed that Sc0.04Ce0.12Zr0.84O1.98 (4S12CZ) and Sc0.04Ce0.16Zr0.80O1.98 (4S16CZ) ceramic materials still maintained stable tetragonal phase structure after 100 h high temperature treatment at 1500 °C. SCZ had a high thermal expansion coefficient (TEC), low thermal conductivity, and high fracture toughness. The TEC of the ceramics increased with CeO2 addition because lattice energy reduced with increasing substitution of Zr4+ by bigger Ce4+ while thermal conductivity decreased due to the increase of lattice distortion. Compared with 4S12CZ, 4S16CZ exhibited a higher fracture toughness of 6.48 ± 0.04 MPa m1/2 and showed the better anti-sintering property. Besides, the thermal conductivity, TEC and thermal cycling lifetime of 4S16CZ were optimal. The comprehensive performance of 4S16CZ suggested it could be explored as a promising TBC material for high-temperature application.
materials science, ceramics