Quantitative Evaluation of Deformation Mechanisms in Austenitic Hadfield Steel under Different Strain Rates
Mahmoud Khedr,Wei Li,Na Min,Ammar. H. Elsheikh,Xuejun Jin
DOI: https://doi.org/10.1002/srin.202400714
IF: 2.1258
2024-12-14
steel research international
Abstract:This study examines the tensile behavior of Hadfield steel under varying strain rates, quantifying the roles of dislocations, mechanical twinning, and dynamic strain aging (DSA) in flow stress. Rising strain rates increase dislocation density, twin volume fraction, and dimple features on fracture surfaces, enhancing both strength and ductility. Forest hardening dominates at higher strain rates, while DSA effects decrease. An austenitic Hadfield steel (1.13% C and 12.45% Mn) is tensile tested under different strain rates (10−5, 10−3, and 10−1 s−1) to quantitatively evaluate the contribution of different deformation mechanisms to the flow stress. Dislocation densities are determined through X‐ray diffraction, twin plates characteristics are assessed via transmission electron microscopy, and dynamic strain aging (DSA) is estimated based on carbon concentration revealed by 3D atomic probe tomography. The results indicate a rise in dislocation density, twin volume fraction, and twin plates width with rising strain rates, while DSA exhibits a decrease. Furthermore, no contribution of strain‐induced martensite is observed. At 10−5 s−1, the contribution of forest hardening induced by dislocations, mechanical twining, and DSA recorded ≈300, 400, and 60 MPa, respectively, whereas the respective values at 10−1 s−1 were ≈560, 510, and 6 MPa. Scanning electron microscope analysis of fracture surfaces reveals an increase in dimple features with increasing strain rate, attributed to the concurrent enhancement of strength and ductility.
metallurgy & metallurgical engineering