Dislocation-Source Hardening In Nanostructured Steel Produced By Severe Plastic Deformation

Naoya Kamikawa,Xiaoxu Huang,Niels Hansen

DOI: https://doi.org/10.4028/www.scientific.net/MSF.638-642.1959

2010-01-01

Abstract:Annealing-induced hardening and deformation-induced softening behavior has recently been found in nanostructured aluminum (fcc) produced by severe plastic deformation. It has also been demonstrated that annealing led to a decrease in ductility while deformation led to an increase in ductility. These mechanical responses are totally opposite to those in conventional coarse-grained samples The present study explores the effect of post-process annealing or deformation on mechanical properties of nanostructured interstitial free (IF) steel (bcc) Accumulative roll-bonding was used to produce the nanostructured IF steel. The deformation structure was characterized by a lamellar boundary structure with a mean spacing of about 200 nm, consisting of high-angle boundaries, low-angle dislocation boundaries and dislocations in the volume between the boundaries When the deformed sample was annealed at 400 degrees C for 0 5 h, the yield stress and ultimate tensile strength increased and the elongation to failure decreased markedly In contrast, when the annealed treatment was followed by a light rolling deformation of 15 % thickness reduction, the strength decreased and the elongation to failure increased These results are consistent with those observed in the aluminum samples Structural observations by transmission electron microscopy indicated that a removal of dislocations between the boundaries leads to a lack of dislocation sources, resulting in a higher stress to activate alternative dislocation sources. It was suggested that deformation rather than annealing could be a new route to improve the ductility of nanostructured metals and that a moderate light deformation gives a good balance of strength and ductility