Influence of partial cobalt-ion substitution on the microstructure and dielectric properties of (Zn0.7Mg0.3)1-xCoxTiO3 ceramics

Xiaodong Xie,Xiaoli Tang,Yulan Jing,Huaiwu Zhang,Hua Su,Yuanxun Li

DOI: https://doi.org/10.1016/j.ceramint.2018.04.140

IF: 5.532

2018-01-01

Ceramics International

Abstract:In this study, cobalt-ion substitution was applied to improve the microstructure and microwave dielectric properties of (Zn0.7Mg0.3)1-xCoxTiO3 ceramics. (Zn0.7Mg0.3)1-xCoxTiO3 ceramics were obtained via the conventional solid-state route, and Li2O:B2O3:SiO2:CaO:Al2O3 (LBSCA) glass was used as a sintering aid to decrease the sintering temperature to 900 °C. X-ray diffraction analysis indicated that (Zn, Mg, Co)TiO3 was the main crystalline phase. Scanning electron microscopy showed that proper cobalt-ion substitution promoted the densification and homogeneity of crystal grains in the (Zn0.7Mg0.3)1-xCoxTiO3 system. At x = 0.075, the sample sintered at 900 °C with 1 wt% LBSCA glass formed a dense microstructure and exhibited excellent microwave dielectric properties of εr = 21.602, Q×f = 80,040 GHz and τf = −70.24 ppm/°C.