Ratcheting Effect of Reinforced Graphite Sheet with Stainless Steel Insert (RGSWSSI) under Cyclic Compression at Elevated Temperature

X. T. Zheng,W. C. Dai,H. F. Chen,J. Shen

DOI: https://doi.org/10.1111/ffe.12847

IF: 3.373

2018-01-01

Fatigue & Fracture of Engineering Materials & Structures

Abstract:Ratcheting and creep of reinforced graphite sheet with stainless steel insert (RGSWSSI) are tested under cyclic stress-controlled compression by a self designed clamp from 500 degrees C to 600 degrees C. The effects of insert type, temperature, stress amplitude, stress rate, creep, and loading sequence are considered. Results present that ratcheting deformations for RGSWSSI with 316-L stainless steel tanged and bonded insert approach to each other and show little rate dependence, while they slightly increase with the increment of stress amplitude and temperature. Moreover, obvious ratcheting effect takes place under cyclic pulsating loads with the peak stress of 32 MPa at 500 degrees C or higher. The accumulated deformations of RGSWSSI under small stress amplitude only increase during about the first 25 cycles and then always turn to shakedown. It can also be estimated by the corresponding static creep strain in practical engineering with good accuracy at high temperature. This work provides important data and understanding of RGSWSSI under harsh fluctuating loads. Highlights 1. Accumulated deformations of 5 different types of RGSWSSI are tested under cyclic compression from 500 degrees C to 600 degrees C. 2. The ratcheting strain, compressive moduli, and creep of RGSWSSI are stressed. 3. The effects of insert type, temperature, stress amplitude, stress rate, creep, and loading sequence are considered. 4. The specimens with tanged insert and bonded insert have very similar mechanical feature under the same load.