Abstract:In this study, Na as the n‐type dopant is introduced in the polycrystalline Bi2Te3 material for enhancing the thermoelectric and mechanical properties. Benefitting from the synergistic optimization of electrical and thermal transport properties, a maximum ZT value of 1.03 is achieved at 303 K for the Bi2Te3‐0.25 wt% sample, which is 70% higher than that of the pristine sample. The recent growing energy crisis draws considerable attention to high‐performance thermoelectric materials. n‐type bismuth telluride is still irreplaceable at near room temperature for commercial application, and therefore, is worthy of further investigation. In this work, nanostructured Bi2Te3 polycrystalline materials with highly enhanced thermoelectric properties are obtained by alkali metal Na solid solution. Na is chosen as the cation site dopant for n‐type polycrystalline Bi2Te3. Na enters the Bi site, introducing holes in the Bi2Te3 matrix and rendering the electrical conductivity tunable from 300 to 1800 Scm–1. The solid solution limit of Na in Bi2Te3 exceeds 0.3 wt%. Owing to the effective solid solution, the Fermi level of Bi2Te3 is properly regulated, leading to an improved Seebeck coefficient. In addition, the scattering of both charge carriers and phonons is modulated, which ensured a high‐power factor and low lattice thermal conductivity. Benefitting from the synergistic optimization of both electrical and thermal transport properties, a maximum figure of merit (ZT) of 1.03 is achieved at 303 K when the doping content is 0.25 wt%, which is 70% higher than that of the pristine sample. This work disclosed an effective strategy for enhancing the performance of n‐type bismuth telluride‐based alloy materials.

High Thermoelectric Performance of N-Type Bi2Te2.7Se0.3via Nanostructure Engineering

Experimental Studies on Anisotropic Thermoelectric Properties and Structures of N-Type Bi2Te2.7Se0.3.

Broad-Temperature Thermoelectric Figure of Merit Enhancement in Unconventional n-Type Bi2Te2.3Se0.7 Alloys

Achieving High Thermoelectric Performance Through Constructing Coherent Interfaces and Building Interface Potential Barriers in N-Type Bi2Te3/Bi2Te2.7Se0.3 Nanocomposites

Isotropic Thermoelectric Performance of Layer-Structured n-Type Bi2Te2.7Se0.3 by Cu Doping

Tunable Electrical Conductivity and Simultaneously Enhanced Thermoelectric and Mechanical Properties in n-type Bi<sub>2</sub>Te<sub>3</sub>

Broad-Temperature Thermoelectric Figure of Merit Enhancement in Unconventional n-Type Bi 2 Te 2.3 Se 0.7 Alloys

Thermoelectric Performance Enhancement in N -Type Bi 2 (tese) 3 Alloys Owing to Nanoscale Inhomogeneity Combined with a Spark Plasma-Textured Microstructure

High thermoelectric and mechanical performance in strong-textured n-type Bi2Te2.7Se0.3 by temperature gradient method

High-Performance p-Type Bi 2 Te 3 -Based Thermoelectric Materials Enabled via Regulating Bi-Te Ratio

Isotropic Thermoelectric Performance of Layer-Structured n-Type Bi 2 Te 2.7 Se 0.3 by Cu Doping

Preparation and Thermoelectric Properties of N -Type Bi 2 Te 2.7 Se 0.3 :D M

Attaining Ultrahigh Thermoelectric Performance of Direction-Solidified Bulk N-Type Bi2Te2.4Se0.6 Via Its Liquid State Treatment

Enhanced Near-Room Temperature Thermoelectric Performance and Mechanical Strength of N-Type BiTeSe Materials Incorporated with Ag2Se Inclusions

Enhanced Thermoelectric Performance of Nanostructured Bi2Te3 Through Significant Phonon Scattering

Tunable Electrical Conductivity and Simultaneously Enhanced Thermoelectric and Mechanical Properties in n‐type Bi2Te3

Enhanced Thermoelectric Performance in N-Type Bi2Te3-Based Alloys Via Suppressing Intrinsic Excitation.

Rare Earth Ytterbium Enhanced Thermoelectric Properties of P-Type Bi0.5Sb1.5Te3

Achieving N- and P-Type Thermoelectric Materials with the Identical Chemical Composition BiSbTe1.5Se1.5 by Defect Structure Engineering

Comprehensive Insight into p -Type Bi 2 Te 3 -Based Thermoelectrics near Room Temperature

Thermoelectric performance of p-type (Bi,Sb)2Te3 incorporating amorphous Sb2S3 nanospheres