Abstract:Abstract 2A12 aluminum alloy had the advantages of light weight and high strength. It could be used to manufacture the skin of the hypersonic aircraft. Due to the thermal deformation of fuselage and wing under long-term thermal and mechanical load, the accuracy of flight control was reduced. The shape memory effect of NiTi shape memory alloy (SMA) could be used to reduce the thermal deformation by realizing the laser welding of NiTi SMA and 2A12 aluminum alloy. According to previous studies on laser welding of NiTi SMA and TC4, the tendency to crack for the welded joints could be reduced by placing the laser beam on the side of TC4. Therefore, TC4 wire was used as the filling material. As the TC4 wire was constantly sent into the molten pool to absorb laser energy, the melting amount of NiTi SMA and 2A12 aluminum alloy were reduced. It was beneficial to reduce the formation of brittle intermetallic compounds. There were mainly the fusion zone (FZ), NiTi SMA/FZ interface, and the 2A12 aluminum alloy/FZ interface in the welded joints. With the increase of laser power, the growing distance of Ti 2 Ni phase also increased. In addition, the Ti-Al intermetallic compounds and the fracture load of joints firstly increased and then decreased. When the laser power was high, Ni-Al intermetallic compounds increased. This caused the decrease of fracture load of welded joints. Besides, pores caused by the burning of elements in the FZ would also weaken the fracture load of welded joints. When the laser power was 2.4 kW, more Ti-Al intermetallic compounds appeared at the interface and the maximum fracture load of welded joint was 211 N mm −1 . The fracture mode was intergranular brittle fracture. The heat affected zone (HAZ) with optimal mechanical properties basically retained the shape memory effect of NiTi SMA.

Laser Welding of Cu-Al-Be Shape Memory Alloys: Microstructure and Mechanical Properties

Dissimilar Laser Welding of Superelastic NiTi and CuAlMn Shape Memory Alloys

Improvement of Damping Properties in Laser Processed Superelastic Cu-Al-Mn Shape Memory Alloys

Laser Welding of Niti Shape Memory Alloy Wires and Tubes for Multi-Functional Design Applications

Dissimilar Laser Welding of a NiTi Shape Memory Alloy to Ti2AlNb

Effect of Laser Welding on Microstructure and Mechanical Behavior of Ni-49at%Ti

Dissimilar laser welding of NiTi shape memory alloy and copper

Process-microstructure-properties of CuAlNi Shape Memory Alloys Fabricated by Laser Powder Bed Fusion

Microstructure, Mechanical Properties and Corrosion Performance of Laser-Welded NiTi Shape Memory Alloy in Simulated Body Fluid

Shape Memory Characteristics in Welded SMA Alloys

Microstructure and Properties of Laser Welded Joint of TiNiNb Wide Hysteresis Shape Memory Alloy

Study on interface and mechanical property of laser welding of NiTi shape memory alloy and 2A12 aluminum alloy joint with a TC4 wire

Laser Welding Effects on Mechanical and Fatigue Properties of an Al-Cu-Li-Mg-Ag Alloy

Microstructural characteristics and mechanical properties of laser-welded copper and aluminum

Mechanical Properties of Additive Laser-Welded NiTi Alloy

Microstructure and Mechanical Properties of Laser Welded Ti/Al Alloys

Microstructural Characterization and Mechanical Behavior of NiTi Shape Memory Alloys Ultrasonic Joints Using Cu Interlayer.

Microstructures of the Pulsed Laser Welded TiZrBeCuMo Composite Amorphous Alloy Joint

YAG Laser Welding of Shape Memory Alloy

Effect of ultrasonic spot welding on the mechanical behaviour of NiTi shape memory alloys

Influences of Annealing on Mechanical Properties and Shape Memory Effects of Laser Welding Joints of Ni47Ti44Nb9 Alloy