Abstract:Abstract 2A12 aluminum alloy had the advantages of light weight and high strength. It could be used to manufacture the skin of the hypersonic aircraft. Due to the thermal deformation of fuselage and wing under long-term thermal and mechanical load, the accuracy of flight control was reduced. The shape memory effect of NiTi shape memory alloy (SMA) could be used to reduce the thermal deformation by realizing the laser welding of NiTi SMA and 2A12 aluminum alloy. According to previous studies on laser welding of NiTi SMA and TC4, the tendency to crack for the welded joints could be reduced by placing the laser beam on the side of TC4. Therefore, TC4 wire was used as the filling material. As the TC4 wire was constantly sent into the molten pool to absorb laser energy, the melting amount of NiTi SMA and 2A12 aluminum alloy were reduced. It was beneficial to reduce the formation of brittle intermetallic compounds. There were mainly the fusion zone (FZ), NiTi SMA/FZ interface, and the 2A12 aluminum alloy/FZ interface in the welded joints. With the increase of laser power, the growing distance of Ti 2 Ni phase also increased. In addition, the Ti-Al intermetallic compounds and the fracture load of joints firstly increased and then decreased. When the laser power was high, Ni-Al intermetallic compounds increased. This caused the decrease of fracture load of welded joints. Besides, pores caused by the burning of elements in the FZ would also weaken the fracture load of welded joints. When the laser power was 2.4 kW, more Ti-Al intermetallic compounds appeared at the interface and the maximum fracture load of welded joint was 211 N mm −1 . The fracture mode was intergranular brittle fracture. The heat affected zone (HAZ) with optimal mechanical properties basically retained the shape memory effect of NiTi SMA.

Effect of ultrasonic spot welding on the mechanical behaviour of NiTi shape memory alloys

Mechanical and Microstructural Characterization of Ultrasonic Welded NiTiCu Shape Memory Alloy Wires to Silver-Coated Copper Ferrules

Enhancing joint strength: investigating different interlayer effects on Ultrasonic spot–welded NiTi/304 stainless steel

Numerical Simulation of Ultrasonic Spot Welding of Superelastic NiTi Alloys: Temperature Distribution and Deformation Behavior

Study on the effect of double-sided laser welding of NiTi shape memory alloys wire

Dissimilar Laser Welding of a NiTi Shape Memory Alloy to Ti2AlNb

Study on interface and mechanical property of laser welding of NiTi shape memory alloy and 2A12 aluminum alloy joint with a TC4 wire

Mechanical Properties of Additive Laser-Welded NiTi Alloy

Microstructure and mechanical properties of ultrasonic spot welding TiNi/Ti6Al4V dissimilar materials using pure Al coating

Microstructure, Mechanical Properties and Corrosion Performance of Laser-Welded NiTi Shape Memory Alloy in Simulated Body Fluid

High-Strength Dissimilar Welds Between a NiTi Shape Memory Alloy and Titanium Obtained by Intermixing Niobium Using Pulsed Laser Beam Welding

The Influence of Laser Welding Parameters on the Microstructure and Mechanical Property of the As-Jointed NiTi Alloy Wires

High strength welding of NiTi and stainless steel by impact: Process, structure and properties

Study on the junction zone of NiTi shape memory alloy produced by selective laser melting via a stripe scanning strategy

Effect of interlayer addition on microstructure and mechanical properties of NiTi/stainless steel joint by electron beam welding

Microstructure and failure behavior of ultrasonic-assisted resistance spot welded AA6061/Ti6Al4 V joints

Phase Transformation Mechanisms of NiTi Shape Memory Alloy During Electromagnetic Pulse Welding of Al/NiTi Dissimilar Joints

Microstructure and Mechanical Properties of Dissimilar NiTi/Ti6Al4V Joints Via Back-Heating Assisted Friction Stir Welding

Effect of Aging on the Phase Transformation and Mechanical Behavior of Ti36ni49hf15 High Temperature Shape Memory Alloy

Effects of material combination for ultrasonic spot welding on microstructure and strength of Al/Al, Al/Cu, and Al/Ni dissimilar joints

Enhancing microstructural and mechanical characteristics of laser welded NiTi SMA/304 SS lap joints with medium and high entropy alloy fillers