Abstract:To enhance the corrosion resistance, biocompatibility and mechanical durability of biomedical titanium alloys, a novel β-Ta2O5 nanoceramic coating was developed using a double glow discharge plasma technique. The surface morphology, phase composition and microstructure of the as-deposited coating were examined by atomic force microscopy (AFM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The coating exhibits a striated structural pattern along the growth direction, which consists of equiaxed β-Ta2O5 grains, 15-20 nm in diameter in cross-section, showing a strong (001) preferred orientation. The mechanical properties and contact damage resistance of the β-Ta2O5 coating were evaluated by nanoindentation. Additionally, scratch tests were performed to evaluate the adhesion strength between the β-Ta2O5 coating and the Ti-6Al-4V substrate. The β-Ta2O5 coating shows high hardness combined with good resistance to both indentation and scratch damage, thus favoring it for long-term load-bearing application in the human body. Electrochemical behavior of the coating was analyzed in both a 0.9 wt % NaCl solution and Ringer's solution at 37 °C, by various electrochemical analytical techniques, including potentiodynamic polarization, electrochemical impedance spectroscopy, potential of zero charge and Mott-Schottky analysis. Compared with uncoated Ti-6Al-4V and commercially pure tantalum, the β-Ta2O5 coating possesses a more positive Ecorr and lower icorr in both aqueous solutions, which is attributed to the thicker and denser β-Ta2O5 coating that provides more effective protection against corrosive attack. In addition, the β-Ta2O5 coating shows stable impedance behavior over 5 days immersion under both simulated body solutions, corroborated by the capacitance and resistance values extracted from the EIS data. Mott-Schottky analysis reveals that the β-Ta2O5 coating shows n-type semiconductor behavior and its donor density is independent of immersion time in both aqueous solutions. Its donor density is of the order of 1 × 1019 cm-3, which is an order of magnitude less than that of the passive films formed on either commercially pure Ta or uncoated Ti-6Al-4V. Moreover, according to the differences between corrosion potential and potential of zero charge, the β-Ta2O5 coating exhibits a greater propensity to repulse chloride ions than both commercially pure Ta and uncoated Ti-6Al-4V. Therefore, the newly developed coating could be used to protect the surface of biomedical titanium alloys under harsh conditions.

Tantalum Coating Prepared by APCVD and In-Vivo Biological Evaluation

Evaluation of Sustained Drug Release Performance and Osteoinduction of Magnetron-Sputtered Tantalum-Coated Titanium Dioxide Nanotubes.

Research on the surface characterization, corrosion and bioactivity of nano-featured tantalum coating on selective electron beam melted Ti6Al4V alloy

Micro-nano porous structured tantalum-coated dental implants promote osteogenic activity in vitro and enhance osseointegration in vivo

Mechanical, Electrochemical, and Osteoblastic Properties of Gradient Tantalum Coatings on Ti6Al4V by Prepared Plasma Alloying Technique

Study on Deposition of Biomedical Ta Coating on Ti6Al4V Alloy Substrate by CVD and Its Properties

Biological and Biomechanical Behavior of Titanium Implants with Fluoridated Hydroxyapatite Coatings

Low-Temperature Deposition of Bioactive Crystalline Titania Films: Effects of Tantalum

Tantalum-incorporated hydroxyapatite coating on titanium implants: its mechanical and in vitro osteogenic properties

Tantalum Coated NiTi Alloy by PIIID for Biomedical Application

Biological activity of tantalum oxide coating doped with calcium and strontium by micro-arc oxidation under osteoimmunomodulation

Micro structured Ti- scaffold decorated with Tantalum based amphiphilic assembly for improved biocompatibility, corrosion resistance and bactericidal characteristics

Preparation of tantalum-containing coatings on NiTi shape memory alloys with enhanced in vitro cytocompatibility and antibacterial effectiveness

Interface interactions between porous titanium/tantalum coatings, produced by Selective Laser Melting (SLM), on a cobalt–chromium alloy

Enhanced antibacterial and osteogenic properties of titanium by sputtering a nanostructured fluoride-doped tantalum oxide coating

Coating of Sandblasted and Acid-Etched Dental Implants With Tantalum Using Vacuum Plasma Spraying

Microstructure and biocompatibility of porous-Ta/Ti-6Al-4 V component produced by laser powder bed fusion for orthopedic implants

Electrochemical Properties of a Novel Β-Ta2o5 Nanoceramic Coating Exposed to Simulated Body Solutions.

Magnesium-incorporated sol-gel Ta2O5 coating on Ti6Al4V and in vitro biocompatibility

Osteoinduction Evaluation of Fluorinated Hydroxyapatite and Tantalum Composite Coatings on Magnesium Alloys

Tantalum coating inhibits Ni-migration from titanium out-diffusion in NiTi shape memory biomedical alloy