Abstract:Silicon carbon nitride thin films were deposited on Co-Cr alloy under varying deposition conditions such as sputtering power and the partial pressure ratio of N(2) to Ar by radio frequency and direct current magnetron sputtering techniques. The chemical bonding configurations, surface topography and hardness were characterized by means of X-ray photoelectron spectroscopy, atomic force microscopy and nano-indentation technique. The sputtering power exhibited important influence on the film composition, chemical bonding configurations and surface topography, the electro-negativity had primary effects on chemical bonding configurations at low sputtering power. A progressive densification of the film microstructure occurring with the carbon fraction was increased. The films prepared by RF magnetron sputtering, the relative content of the Si-N bond in the films increased with the sputtering power increased, and Si-C and Si-Si were easily detachable, and C-O, N-N and N-O on the film volatile by ion bombardment which takes place very frequently during the film formation process. With the increase of sputtering power, the films became smoother and with finer particle growth. The hardness varied between 6 GPa and 11.23 GPa depending on the partial pressure ratio of N(2) to Ar. The tribological characterization of Co-Cr alloy with Si-C-N coating sliding against UHMWPE counter-surface in fetal bovine serum, shows that the wear resistance of the Si-C-N coated Co-Cr alloy/UHMWPE sliding pair show much favourable improvement over that of uncoated Co-Cr alloy/UHMWPE sliding pair. This study is important for the development of advanced coatings with tailored mechanical and tribological properties. Crown Copyright (C) 2011 Published by Elsevier B.V. All rights reserved.

Improving the Mechanical Property of Amorphous Carbon Films by Silicon Doping

Structural and tribological behaviours of silicon doped amorphous carbon films

Influence of Si on the Microstructure and Mechanical and Tribological Properties of Ag/a-C:H Films

Tribology dependence on both structures of bulk a-C:H:Si films and transfer layer via adjustable Si content

Achieving superlubricity and high adhesion strength of hydrogenated amorphous carbon film with Al/Cr/Si-doping

Microstructure, mechanical and high-temperature tribological properties of amorphous SiC films by pulsed magnetron sputtering

Tribological Behavior of MoS2/a-C:Si Composite Films in High-Temperature Air and Vacuum Environments

The Structure, Surface Topography and Mechanical Properties of Si–C–N Films Fabricated by RF and DC Magnetron Sputtering

The Influence of Radio Frequency Power on the Characteristics of Carbon-Rich Hydrogenated Amorphous Silicon Carbide Films

Microstructure, Mechanical Properties and Wetting Behavior of F: Si–C–N Films As Bio-Mechanical Coating Grown by DC Unbalanced Magnetron Sputtering

Effects of silicon doping on low-friction and high-hardness diamond-like carbon coating via filtered cathodic vacuum arc deposition

Tribological behavior of MoS 2 /a-C:Si composite films in high-temperature air and vacuum environments

Effect of silicon-doping on the wide-temperature tribological behavior and lubrication mechanism of WC/a-C film

Microstructure, Mechanical and Tribological Properties of Si and Al Co-Doped Hydrogenated Amorphous Carbon Films Deposited at Various Bias Voltages

Influence of C Dopant on the Structure, Mechanical and Tribological Properties of R.F.-Sputtered Mos2/A-C Composite Films

Effect of Si Content on the Tribological Properties of Crsin Films in Air and Water Environments

Structure and Tribological Behavior of Amorphous Carbon Films Implanted with Cr+ Ions

Preparation of CrSiN-Ag Films and Evaluation of Their Properties

The role of Si on the structure and tribological properties of a-C:H:Ni soft films at elevated temperatures

Annealing Effect on Optical and Electronic Properties of Silicon Rich Amorphous Silicon-Carbide Films

Modification of a-C:H films via nitrogen and silicon doping: The way to the superlubricity in moisture atmosphere