Abstract:Successful preparation of photopolymerizable ceramic slurries using non-oxide ceramics and their 3D printing is highly challenging as the ceramic powders often possess high UV-light absorbance. Even though pre-oxidation of the powders could improve the slurry printability, the residual oxygen element in the material would eventually deteriorate the material purity and performance. In this study, a separated redox route (pre-oxidation, 3D printing and carbothermal reduction) was proposed to overcome these challenges. SiC ceramic powder was pre-oxidized into SiC@SiO2 core-shell form to lower the UV-light absorbance. It was found that the ultraviolet (UV) light absorbance value of SiC powder at 405 nm decreased 20% from 0.357 to 0.284 after pre-oxidation process. The UV-light penetration depth of SiC@SiO2 ceramic slurries at 40 similar to 55 vol% solid loading ranging from 14.81 to 12.82 mu m, which surpassed two times that for 40 vol% raw SiC ceramic slurry. Different-shaped structures of SiC@SiO2/resin green ceramic bodies were successfully fabricated by vat photopolymerization 3D printing. The oxygen element resided was then eliminated by carbothermal reduction to avoid detriment of SiO2 to the mechanical performance of the SiC ceramics. Phenolic epoxy acrylate resin with 14 wt% pyrolytic carbon (PyC) yield was chosen as the carbon source and thus the SiC@SiO2/resin green body pyrolyzed into SiC@SiO2/PyC ceramics after 1200 degrees C. It was found that after the heating temperature was further raised to 1600 degrees C, most of the pre-introduced SiO2 shells on the surface of SiC particles were in situ transformed into SiC nanowires through carbothermal reduction reaction between SiO2 and PyC, and the content of oxygen element in the ceramic matrix sharply dropped from 20.21% to 2.08%. The results demonstrated that through the proposed redox route, the photopolymerization-related issues including high UV-light absorbance and pre-oxidation-induced impurity for 3D printing of SiC ceramic slurries can be tackled. Finally, high purity porous SiCnw/SiC ceramic components with different structures were produced. This study provides a promising route for the preparation and 3D printing of photopolymerization ceramic slurries using non-oxide ceramics possessing high UV-light absorbance.

Fabrication of Si2N2O Ceramic with Silicon Kerf Waste As Raw Material

Fabricating superior thermal conductivity SiC–AlN composites from photovoltaic silicon waste

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Green synthesis of porous SiC ceramics using silicon kerf waste in different sintering atmospheres and pore structure optimization

Self-assembling of versatile Si3N4@SiO2 nanofibre sponges by direct nitridation of photovoltaic silicon waste

Waste Conversion into High-Value Ceramics: Carbothermal Nitridation Synthesis of Titanium Nitride Nanoparticles Using Automotive Shredder Waste.

Recycling of kerf loss silicon: An optimized method to realize effective elimination of various impurities

Recycling of silicon from waste PV diamond wire sawing silicon powders: A strategy of Na2CO3-assisted pressure-less sintering and acid leaching

Efficient Preparation of Si3N4 by Microwave Treatment of Solar-Grade Waste Silicon Powder

Fabrication and properties of Si2N2O-Si3N4 ceramics via direct ink writing and low-temperature sintering

Fabrication of continuously porous SiC–Si3N4 composite using SiC powder by extrusion process

Sustainable synthesis of silicon carbide from sludge waste generated in organosilane industry

3D Printing and in Situ Transformation of SiCnw/SiC Structures

Al2O3 and CaO As Sintering Aids: A Strategy to Remove Impurity Boron and SiO2 Surface-Layer of Diamond Wire Saw Silicon Waste

Fabrication of Porous Silicon Nitride with High Porosity by Diatomite

Recycle of silicon slurry cutting waste to prepare high purity SiC by salt-assisted carbothermic reduction

Fabrication and characterization of silicon carbide ceramic filtration media via recycling of waste red mud

SiC Generation Mechanism in Photovoltaic Crystal Pulling Waste Graphite Infusion Cylinder

Fabrication and Properties of SiC Porous Ceramics by Slip Casting Process

The Synthesis Of Nanostructured Sic From Waste Plastics And Silicon Powder

Study on In-Situ Reaction Synthesis and Mechanical Properties of Si2N2O Ceramic