Abstract:High engineering critical current density JE of >500 A/mm2 at 20 T and 4.2 K can be regularly achieved in Ag-sheathed multifilamentary Bi2Sr2CaCu2Ox (Bi-2212) round wire when the sample length is several centimeters. However, JE(20 T) in Bi-2212 wires of several meters length, as well as longer pieces wound in coils, rarely exceeds 200 A/mm2. Moreover, long-length wires often exhibit signs of Bi-2212 leakage after melt processing that are rarely found in short, open-end samples. We studied the length dependence of JE of state-of-the-art powder-in-tube (PIT) Bi-2212 wires and gases released by them during melt processing using mass spectroscopy, confirming that JE degradation with length is due to wire swelling produced by high internal gas pressures at elevated temperatures [1,2]. We further modeled the gas transport in Bi-2212 wires and examined the wire expansion at critical stages of the melt processing of as-drawn PIT wires and the wires that received a degassing treatment or a cold-densification treatment before melt processing. These investigations showed that internal gas pressure in long-length wires drives creep of the Ag sheath during the heat treatment, causing wire to expand, lowering the density of Bi-2212 filaments, and therefore degrading the wire JE; the creep rupture of silver sheath naturally leads to the leakage of Bi-2212 liquid. Our work shows that proper control of such creep is the key to preventing Bi-2212 leakage and achieving high JE in long-length Bi-2212 conductors and coils.

Uniaxial Strain Induced Critical Current Degradation of Ag-Sheathed Bi-2212 Round Wire

The Axial Tensile Stress–Strain Characterization of Ag-Sheathed Bi2212 Round Wire

Influence of Torsional Strain on the Bi-2212 Tapes and Round Wires under Background Field

Damage Behavior in Bi-2212 Round Wire with 3D Elastoplastic Peridynamic

Tensile strain effects on critical current of Ag and Ag alloy-sheathed Bi-2223 superconducting tapes

Critical Current under Uniaxial Strain on High-Pressure Heat Treatment Bi-2212 Round Wire

Degradation of Critical Current in Bi2212 Composite Wire under Compression Load

Axial Tensile Stress-Strain Characterization Of Bi-2212 Round Wire With Different Heat Treatments

Mechanical Behavior in Superconducting Composite Wires

Critical current of Bi-2212 round wires with different heat treatment conditions

Performance and Microstructure of Bi-2212 Wire under Different OverPressures Heat-treatment

Role of internal gases and creep of Ag in controlling the critical current density of Ag-sheathed Bi2Sr2CaCu2Ox wires

Critical Current Degradation Caused By Winding Process Of Bi-2223/Ag Hts Wire In The Form Of A Coil

Stress–Strain Distribution Analysis in Bi2212 Subcable Based on Numerical Modeling and Experiment

Microstructure and Critical Current Density of Bi-2212 Single- and Multi-filamentary Wires with Overpressure Heat Treatment Processing

The Critical Current Degradation of Bi-2223 Superconducting Tapes Due to Fatigue Cycles at Different Strain Range

Influence of Sheath Materials on the Strain Tolerance of Bi-2223 Superconducting Tapes

Evidence for length-dependent wire expansion, filament dedensification and consequent degradation of critical current density in Ag-alloy sheathed Bi-2212 wires

Protocols and methodologies for acquiring and analyzing critical-current versus longitudinal-strain data in Bi2Sr2CaCu2O8+x wires

The effects of bending strain on the critical current and alternating loss of Bi2223HTS tapes

Strain Effect on Critical Current Degradation in Bi-Based Superconducting Tapes with Different Deformation Modes