Microstructure Evolution and Compressive Property Variation of CoCrFeNiAlx High Entropy Alloys Produced by Directional Solidification
Zhuhuan Yu,Xiong Yang,Yawen Yan,Xiaohui Wang,Xuliang Liu,Wei Du,Zi Yang
DOI: https://doi.org/10.1007/s11837-024-06576-5
2024-05-08
JOM
Abstract:CoCrFeNiAl x ( x = 0.3, 0.6, 0.9 and 1.2, molar ratio) high-entropy alloys (HEAs) were prepared by directional solidification at the withdrawal rate of 70 μm/s and were simply referred to as Al 0.3 , Al 0.6 , Al 0.9 and Al 1.2 alloy, respectively. The effects of Al content on microstructure evolution, component segregation and compressive property of these alloys were investigated. The study revealed that increasing Al content induced a transition from face-centered cubic (FCC) to body-centered cubic (BCC) crystal structure. Simultaneously, the microstructure transformed from coarse irregular dendrites to equiaxed dendrites and the morphology of the solid-liquid interface changed from cellular dendrites to dendrites. Specifically, the Al 0.3 alloy exhibited the single FCC phase, while the Al 0.6 alloy consisted of dendritic FCC of phase CoCrFe-enriched and inter-dendritic BCC phase of AlNi-enriched. The Al 0.9 and Al 1.2 alloys showed AlNi-enriched precipitate B2 phase and CoCrFe-enriched matrix FCC phase. As the Al content increased, the CoCrFeNiAl x HEAs ultimate compressive strength initially increased and then decreased. The Al 0.9 alloy achieved the supreme ultimate compressive strength of 2265.17 MPa, attributed to crystal structure transformation and solid solution strengthening. Additionally, the compressive strain consistently decreased with increasing Al content, reaching the minimum of 23.46% for the Al 1.2 alloy.
materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing,mineralogy