Abstract:A series of nitrogen-doped carbons were prepared by using biomass waste sawdust as carbon source for supercapacitors. A new nitrogen-doping strategy was proposed to introduce nitrogen element into carbons by using ethylenediamine and carbon as nitrogen source through the polymerization reaction on sawdust under moderate conditions. The raw carbons were further activated with KOH to improve the surface area to increase the electric double layer capacitance while the heteroatoms can improve the pseudocapacitance. The prepared carbons were characterized with different techniques and the electrochemical performances were tested. It was found that the nitrogen-doped carbons activated with a KOH to carbon mass ratio of 5 (NC600-800-5) has the largest specific surface area (1674 m(2)g(-1)) and moderate nitrogen content (2.88 wt%). Compared with the carbon without introduction of nitrogen element (C600-800-5), the capacitive performances of nitrogen-doped carbons were greatly improved, which may be due to the increase of pseudocapacitance and the improvement of wettability introduced by nitrogen element. The largest specific capacitance, 367 F g(-1), was reached at 0.5 A g(-1 )in 6 M KOH solution while the specific capacitance of C600-800-5 is only 279 F g(-1). After 10,000 cycles at 3 A g(-1), the specific capacitance can keep 96.7% of the initial value, suggesting the excellent cycling performance. The energy density can reach 8.7 Wh Kg(-1) at a power density of 251.6 W kg(-1). Thus, it is proved that the nitrogendoping strategy is effective and the introduction of nitrogen element to carbons is particularly important to the improvement of the electrochemical performances.

Nitrogen and Oxygen Co-Doped Porous Carbon for High Performance Supercapacitors

Nitrogen-functionalized Microporous Carbon Nanoparticles for High Performance Supercapacitor Electrode

Highly N/O co-doped ultramicroporous carbons derived from nonporous metal-organic framework for high performance supercapacitors

Water bamboo-derived porous carbons as electrode materials for supercapacitors

Nitrogen-Doped Porous Carbons Through Koh Activation with Superior Performance in Supercapacitors

N/O Co-Enriched Amorphous Carbon Coated Graphene with a Sandwiched Porous Architecture As Supercapacitor Electrodes with High Volumetric Specific Capacitance

Nitrogen and Phosphorus Co-doped Porous Carbon for High-Performance Supercapacitors

One-Step Synergistic Effect to Produce Two-Dimensional N-Doped Porous Carbon Nanosheets with Ultrahigh Porosity from Biomass for High-Performance Supercapacitors

Nitrogen-doped Hierarchical Porous Carbon Microsphere Through KOH Activation for Supercapacitors.

Synthesis of Nitrogen-Doped Porous Carbon Nanofibers As an Efficient Electrode Material for Supercapacitors.

N/O Co-Doped Hierarchically Porous Carbon with Three-Dimensional Conductive Network for High-Performance Supercapacitors

Formation of CoO-NiO Nanoparticles on Nitrogen Doped Porous Carbon as High Performance Supercapacitor Electrode

Facile Synthesis of Nitrogen-Doped Porous Carbons for CO 2 Capture and Supercapacitors

Template-free Preparation of Nitrogen-Doped Activated Carbon with Porous Architecture for High-Performance Supercapacitors

Nitrogen Doping of Porous Carbon Electrodes Derived from Pine Nut Shell for High-Performance Supercapacitors

N-doped Carbons with Hierarchically Micro- and Mesoporous Structure Derived from Sawdust for High Performance Supercapacitors

Three-dimensional Nitrogen-Doped Hierarchical Porous Carbon Derived from Cross-Linked Lignin Derivatives for High Performance Supercapacitors

Porous oxygen-doped NiCoP nanoneedles for high performance hybrid supercapacitor

Nitrogen-Doped Porous Carbons Derived from Peanut Shells as Efficient Electrodes for High-Performance Supercapacitors

Organic Crosslinked Polymer-Derived N/O-Doped Porous Carbons for High-Performance Supercapacitor

Facile 3D Nitrogen‐Doped Hierarchical Porous Carbon for High‐Performance Supercapacitors